Effect of chain extending cross-linkers on the disintegration behavior of composted PBAT/PLA blown films

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F23%3A63566898" target="_blank" >RIV/70883521:28110/23:63566898 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/70883521:28610/23:63566898

Výsledek na webu

<a href="https://www.mdpi.com/1422-0067/24/5/4525" target="_blank" >https://www.mdpi.com/1422-0067/24/5/4525</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ijms24054525" target="_blank" >10.3390/ijms24054525</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of chain extending cross-linkers on the disintegration behavior of composted PBAT/PLA blown films

Popis výsledku v původním jazyce

A biodegradable blend of PBAT—poly(butylene adipate-co-terephthalate)—and PLA—poly(lactic acid)—for blown film extrusion was modified with four multi-functional chain extending cross-linkers (CECL). The anisotropic morphology introduced during film blowing affects the degradation processes. Given that two CECL increased the melt flow rate (MFR) of tris(2,4-di-tert-butylphenyl)phosphite (V1) and 1,3-phenylenebisoxazoline (V2) and the other two reduced it (aromatic polycarbodiimide (V3) and poly(4,4-dicyclohexylmethanecarbodiimide) (V4)), their compost (bio-)disintegration behavior was investigated. It was significantly altered with respect to the unmodified reference blend (REF). The disintegration behavior at 30 and 60 °C was investigated by determining changes in mass, Young’s moduli, tensile strengths, elongations at break and thermal properties. In order to quantify the disintegration behavior, the hole areas of blown films were evaluated after compost storage at 60 °C to calculate the kinetics of the time dependent degrees of disintegration. The kinetic model of disintegration provides two parameters: initiation time and disintegration time. They quantify the effects of the CECL on the disintegration behavior of the PBAT/PLA compound. Differential scanning calorimetry (DSC) revealed a pronounced annealing effect during storage in compost at 30 °C, as well as the occurrence of an additional step-like increase in the heat flow at 75 °C after storage at 60 °C. The disintegration consists of processes which affect amorphous and crystalline phase of PBAT in different manner that cannot be understood by a hydrolytic chain degradation only. Furthermore, gel permeation chromatography (GPC) revealed molecular degradation only at 60 °C for the REF and V1 after 7 days of compost storage. The observed losses of mass and cross-sectional area seem to be attributed more to mechanical decay than to molecular degradation for the given compost storage times.

Název v anglickém jazyce

Effect of chain extending cross-linkers on the disintegration behavior of composted PBAT/PLA blown films

Popis výsledku anglicky

A biodegradable blend of PBAT—poly(butylene adipate-co-terephthalate)—and PLA—poly(lactic acid)—for blown film extrusion was modified with four multi-functional chain extending cross-linkers (CECL). The anisotropic morphology introduced during film blowing affects the degradation processes. Given that two CECL increased the melt flow rate (MFR) of tris(2,4-di-tert-butylphenyl)phosphite (V1) and 1,3-phenylenebisoxazoline (V2) and the other two reduced it (aromatic polycarbodiimide (V3) and poly(4,4-dicyclohexylmethanecarbodiimide) (V4)), their compost (bio-)disintegration behavior was investigated. It was significantly altered with respect to the unmodified reference blend (REF). The disintegration behavior at 30 and 60 °C was investigated by determining changes in mass, Young’s moduli, tensile strengths, elongations at break and thermal properties. In order to quantify the disintegration behavior, the hole areas of blown films were evaluated after compost storage at 60 °C to calculate the kinetics of the time dependent degrees of disintegration. The kinetic model of disintegration provides two parameters: initiation time and disintegration time. They quantify the effects of the CECL on the disintegration behavior of the PBAT/PLA compound. Differential scanning calorimetry (DSC) revealed a pronounced annealing effect during storage in compost at 30 °C, as well as the occurrence of an additional step-like increase in the heat flow at 75 °C after storage at 60 °C. The disintegration consists of processes which affect amorphous and crystalline phase of PBAT in different manner that cannot be understood by a hydrolytic chain degradation only. Furthermore, gel permeation chromatography (GPC) revealed molecular degradation only at 60 °C for the REF and V1 after 7 days of compost storage. The observed losses of mass and cross-sectional area seem to be attributed more to mechanical decay than to molecular degradation for the given compost storage times.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10404 - Polymer science

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Molecular Sciences

ISSN

1661-6596

e-ISSN

1422-0067

Svazek periodika

24

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

21

Strana od-do

—

Kód UT WoS článku

000948228800001

EID výsledku v databázi Scopus

2-s2.0-85149821036