Impact behaviour of acrylonitrile-butadiene-styrene after temperature and humidity load
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28140%2F17%3A63517157" target="_blank" >RIV/70883521:28140/17:63517157 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1051/matecconf/201712502048" target="_blank" >http://dx.doi.org/10.1051/matecconf/201712502048</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1051/matecconf/201712502048" target="_blank" >10.1051/matecconf/201712502048</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Impact behaviour of acrylonitrile-butadiene-styrene after temperature and humidity load
Popis výsledku v původním jazyce
This study deals with acrylonitrile-butadiene-styrene (ABS) which was subjected the drop-weight test before and after temperature and humidity load. ABS is an engineering plastic and also an important engineering terpolymer, which has butadiene part uniformly distributed through the acrylonitrile-styrene matrix and is commonly used in production of automotive interior components. The injection moulded ABS samples were subjected the penetration test at fall height 100 J before and after temperature and humidity load and the results were subsequently evaluated and discussed. It was found out that ABS after temperature and humidity load has lower impact resistance.
Název v anglickém jazyce
Impact behaviour of acrylonitrile-butadiene-styrene after temperature and humidity load
Popis výsledku anglicky
This study deals with acrylonitrile-butadiene-styrene (ABS) which was subjected the drop-weight test before and after temperature and humidity load. ABS is an engineering plastic and also an important engineering terpolymer, which has butadiene part uniformly distributed through the acrylonitrile-styrene matrix and is commonly used in production of automotive interior components. The injection moulded ABS samples were subjected the penetration test at fall height 100 J before and after temperature and humidity load and the results were subsequently evaluated and discussed. It was found out that ABS after temperature and humidity load has lower impact resistance.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
MATEC Web of Conferences
ISBN
—
ISSN
2261-236X
e-ISSN
neuvedeno
Počet stran výsledku
4
Strana od-do
"nestrankovano"
Název nakladatele
EDP Sciences
Místo vydání
Les Ulis
Místo konání akce
Heraklion, Crete
Datum konání akce
14. 7. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—