Durability Prediction of NR/BR and NR/SBR Blend Tread Compounds using Tear Fatigue Analyser
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28610%2F16%3A43874325" target="_blank" >RIV/70883521:28610/16:43874325 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Durability Prediction of NR/BR and NR/SBR Blend Tread Compounds using Tear Fatigue Analyser
Popis výsledku v původním jazyce
The present work aims to characterize fatigue crack growth (FCG) behaviour for comparative durability prediction of NR/BR and NR/SBR blend based compounds. The influence of strain, temperature, r-ratio and waveform was studied to simulate realistic service life condition by using aTear and Fatigue Analyser (TFA). Both of these blends shown higher FCG rate at higher temperature, but the effect is comparatively higher in NR/SBR compound. The influence of r-ratio towards FCG rate was found to be very less in NR/BR blend, whereas NR/SBR blend shown considerable decrease in FCG rate at positive r-ratio. The higher FCG rate was observed in pulse mode compared to sine mode in both the blends.
Název v anglickém jazyce
Durability Prediction of NR/BR and NR/SBR Blend Tread Compounds using Tear Fatigue Analyser
Popis výsledku anglicky
The present work aims to characterize fatigue crack growth (FCG) behaviour for comparative durability prediction of NR/BR and NR/SBR blend based compounds. The influence of strain, temperature, r-ratio and waveform was studied to simulate realistic service life condition by using aTear and Fatigue Analyser (TFA). Both of these blends shown higher FCG rate at higher temperature, but the effect is comparatively higher in NR/SBR compound. The influence of r-ratio towards FCG rate was found to be very less in NR/BR blend, whereas NR/SBR blend shown considerable decrease in FCG rate at positive r-ratio. The higher FCG rate was observed in pulse mode compared to sine mode in both the blends.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
V - Vyzkumna aktivita podporovana z jinych verejnych zdroju
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Kautschuk Gummi Kunststoffe
ISSN
0948-3276
e-ISSN
—
Svazek periodika
2016
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
3
Strana od-do
53-55
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—