Tribological Properties of Nanosized Calcium Carbonate Filled Polyamide 66 Nanocomposites

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28610%2F16%3A43874566" target="_blank" >RIV/70883521:28610/16:43874566 - isvavai.cz</a>

Výsledek na webu

<a href="http://scitation.aip.org/content/aip/proceeding/aipcp/10.1063/1.4942299" target="_blank" >http://scitation.aip.org/content/aip/proceeding/aipcp/10.1063/1.4942299</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1063/1.4942299" target="_blank" >10.1063/1.4942299</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Tribological Properties of Nanosized Calcium Carbonate Filled Polyamide 66 Nanocomposites

Popis výsledku v původním jazyce

For the purpose of developing high performance tribomaterials for mechanical sliding parts such as gears, bearings and so on, nanosized calcium carbonate (nano-CaCO3) tilled polyamide 66 (PA66) nanocomposites were investigated. The nano-CaCO3 was a kind of precipitated (colloid typed) CaCO3, and its average particle size was 40, 80 and 150 nm. Surface treatment was performed by fatty acid on the nano-CaCO3 and its volume fraction in the nanocomposite was varied from 1 to 20vol.%. These nanocomposites were melt-mixed by a twin screw extruder and injection-molded. Tribological properties were measured by two types of sliding wear testers such as ring-on-plate type and ball-on-plate type one under dry condition. The counterface, worn surface and wear debris were observed by digital microscope and scanning electron microscope. It was found that the nano-CaCO3 has a good effect on the tribological properties, although the effect on the frictional coefficient and specific wear rate is differed by the volume fraction and the type of sliding wear modes. This is attributed to the change of wear mechanisms, which is the change of form of the transfer films on the counterface and the size of wear debris. It follows from these results that PA66/nano-CaCO3 nanocomposites may be possible to be the high performance tribomaterials.

Název v anglickém jazyce

Tribological Properties of Nanosized Calcium Carbonate Filled Polyamide 66 Nanocomposites

Popis výsledku anglicky

For the purpose of developing high performance tribomaterials for mechanical sliding parts such as gears, bearings and so on, nanosized calcium carbonate (nano-CaCO3) tilled polyamide 66 (PA66) nanocomposites were investigated. The nano-CaCO3 was a kind of precipitated (colloid typed) CaCO3, and its average particle size was 40, 80 and 150 nm. Surface treatment was performed by fatty acid on the nano-CaCO3 and its volume fraction in the nanocomposite was varied from 1 to 20vol.%. These nanocomposites were melt-mixed by a twin screw extruder and injection-molded. Tribological properties were measured by two types of sliding wear testers such as ring-on-plate type and ball-on-plate type one under dry condition. The counterface, worn surface and wear debris were observed by digital microscope and scanning electron microscope. It was found that the nano-CaCO3 has a good effect on the tribological properties, although the effect on the frictional coefficient and specific wear rate is differed by the volume fraction and the type of sliding wear modes. This is attributed to the change of wear mechanisms, which is the change of form of the transfer films on the counterface and the size of wear debris. It follows from these results that PA66/nano-CaCO3 nanocomposites may be possible to be the high performance tribomaterials.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED2.1.00%2F03.0111" target="_blank" >ED2.1.00/03.0111: Centrum polymerních systémů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

C - Předmět řešení projektu podléhá obchodnímu tajemství (§ 504 Občanského zákoníku), ale název projektu, cíle projektu a u ukončeného nebo zastaveného projektu zhodnocení výsledku řešení projektu (údaje P03, P04, P15, P19, P29, PN8) dodané do CEP, jsou upraveny tak, aby byly zveřejnitelné.

Název statě ve sborníku

Proceedings Of Pps-31: The 31St International Conference Of The Polymer Processing Society

ISBN

978-0-7354-1360-3

ISSN

0094-243X

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

American Institute of Physics

Místo vydání

Melville

Místo konání akce

Jeju Island

Datum konání akce

7. 6. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000375945000043