Fatigue behavior of filled rubber material
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28610%2F16%3A43874799" target="_blank" >RIV/70883521:28610/16:43874799 - isvavai.cz</a>
Výsledek na webu
<a href="http://plastko.utb.cz/index.php/sbornik" target="_blank" >http://plastko.utb.cz/index.php/sbornik</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue behavior of filled rubber material
Popis výsledku v původním jazyce
The understanding of the fatigue behavior of rubber in the dependence on the complex stress loading conditions, which is the reason for crack initiations and its propagation, is a subject of high scientific and application oriented interest to understand and improve durability and life service of rubber products. In the present work, the pure rubbers; natural rubber (NR) and butadiene rubber (BR) as well as binary rubber blend NR/BR at the blend ratio 50/50 filled with varied content 10, 30 and 50 phr of carbon black (CB) with commonly encountered rubber additives were subjected to fatigue loading conditions under sinusoidal waveform up to 1.000.000 of loading cycles. The focus was to observe the fatigue behavior of each of the rubber component as well as the rubber blend. This paper describes the fatigue behavior of different rubber materials for describing the influence of strain crystallization as well as of filler content on stress evaluation during increasing number of fatigue cycles.
Název v anglickém jazyce
Fatigue behavior of filled rubber material
Popis výsledku anglicky
The understanding of the fatigue behavior of rubber in the dependence on the complex stress loading conditions, which is the reason for crack initiations and its propagation, is a subject of high scientific and application oriented interest to understand and improve durability and life service of rubber products. In the present work, the pure rubbers; natural rubber (NR) and butadiene rubber (BR) as well as binary rubber blend NR/BR at the blend ratio 50/50 filled with varied content 10, 30 and 50 phr of carbon black (CB) with commonly encountered rubber additives were subjected to fatigue loading conditions under sinusoidal waveform up to 1.000.000 of loading cycles. The focus was to observe the fatigue behavior of each of the rubber component as well as the rubber blend. This paper describes the fatigue behavior of different rubber materials for describing the influence of strain crystallization as well as of filler content on stress evaluation during increasing number of fatigue cycles.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Sborník konference PLASTKO 2016
ISBN
978-80-7454-590-0
ISSN
—
e-ISSN
—
Počet stran výsledku
9
Strana od-do
"neuveden"
Název nakladatele
Univerzita Tomáše Bati ve Zlíně
Místo vydání
Zlín
Místo konání akce
Zlín
Datum konání akce
20. 4. 2016
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—