Magnetorheology of dimorphic magnetorheological fluids based on iron nanorods
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28610%2F17%3A63517029" target="_blank" >RIV/70883521:28610/17:63517029 - isvavai.cz</a>
Výsledek na webu
<a href="http://iopscience.iop.org/article/10.1088/1742-6596/790/1/012031/meta" target="_blank" >http://iopscience.iop.org/article/10.1088/1742-6596/790/1/012031/meta</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1742-6596/790/1/012031" target="_blank" >10.1088/1742-6596/790/1/012031</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Magnetorheology of dimorphic magnetorheological fluids based on iron nanorods
Popis výsledku v původním jazyce
The aim of this paper is to document suitability of partial substitution of magnetic carbonyl iron (CI) microspheres with iron nanorods to obtain dimorphic magnetorheological (MR) suspensions with comparable MR performance to conventional MR suspensions exclusively based on (CI) microspheres while the sedimentation stability is considerably improved. The morphology of CI and iron nanorods was analyzed via scanning electron microscopy and transmission electron microscopy, respectively, and magnetic properties via vibrating sample magnetometry. The steady shear flow and small-amplitude dynamic oscillatory shear measurements were carried out to confirm effective MR performance. The sedimentation test showed positive role of dimorphic composition of dispersed phase on the sedimentation stability.
Název v anglickém jazyce
Magnetorheology of dimorphic magnetorheological fluids based on iron nanorods
Popis výsledku anglicky
The aim of this paper is to document suitability of partial substitution of magnetic carbonyl iron (CI) microspheres with iron nanorods to obtain dimorphic magnetorheological (MR) suspensions with comparable MR performance to conventional MR suspensions exclusively based on (CI) microspheres while the sedimentation stability is considerably improved. The morphology of CI and iron nanorods was analyzed via scanning electron microscopy and transmission electron microscopy, respectively, and magnetic properties via vibrating sample magnetometry. The steady shear flow and small-amplitude dynamic oscillatory shear measurements were carried out to confirm effective MR performance. The sedimentation test showed positive role of dimorphic composition of dispersed phase on the sedimentation stability.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10305 - Fluids and plasma physics (including surface physics)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Journal of Physics: Conference Series (print)
ISBN
—
ISSN
1742-6588
e-ISSN
neuvedeno
Počet stran výsledku
7
Strana od-do
1-7
Název nakladatele
Institute of Physics Publishing Ltd.
Místo vydání
Bristol
Místo konání akce
Lillafured
Datum konání akce
5. 10. 2015
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000400612300031