Determination of Relationship between Chemical Composition of Electrolyte and Surface Sample Quality

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F75081431%3A_____%2F16%3A00000623" target="_blank" >RIV/75081431:_____/16:00000623 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Determination of Relationship between Chemical Composition of Electrolyte and Surface Sample Quality
Popis výsledku v původním jazyce
Paper tracks experimentally confirmed relationship between chemical composition of electrolyte and resulting surface finish quality of created oxide layer during the process of anodic oxidation of aluminium. Examined chemical factors were: concentrations of sulphuric acid, oxalic acid, boric acid and sodium chloride. Aggressive effects of electrolyte were chosen as indicator of resulting layer quality – presence and extent of etching of used substrate sample.
Název v anglickém jazyce
Determination of Relationship between Chemical Composition of Electrolyte and Surface Sample Quality
Popis výsledku anglicky
Paper tracks experimentally confirmed relationship between chemical composition of electrolyte and resulting surface finish quality of created oxide layer during the process of anodic oxidation of aluminium. Examined chemical factors were: concentrations of sulphuric acid, oxalic acid, boric acid and sodium chloride. Aggressive effects of electrolyte were chosen as indicator of resulting layer quality – presence and extent of etching of used substrate sample.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CI - Průmyslová chemie a chemické inženýrství
OECD FORD obor
—

Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)