ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F75081431%3A_____%2F16%3A00000667" target="_blank" >RIV/75081431:_____/16:00000667 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT

Popis výsledku v původním jazyce

In the contribution is evaluated an impact of physical factors of anodizing process, namely the temperature of an electrolyte, anodizing time and voltage, on the change of values of Vickers microhardness and thickness of formed layer of experimental materials Al99-5. By increasing of electrolyte temperature, the values of layer microhardness and thickness layer increase, namely about 0.78 % at the increasing of electrolyte temperature by 1 °C. By lengthening of anodizing time grows the value of layer thickness, but only to the value of the critical deposition time, when chemical dissolution of the layer start to be more prominent. By voltage increasing, values of layer thickness and micro-hardness are increased in the range of the used experimental values.

Název v anglickém jazyce

ANALYSIS OF PHYSICAL FACTORS ON CHOSEN PROPERTIES OF ANODIC ALUMINA OXIDE (AAO) LAYERS AND ENVIRONMENT

Popis výsledku anglicky

In the contribution is evaluated an impact of physical factors of anodizing process, namely the temperature of an electrolyte, anodizing time and voltage, on the change of values of Vickers microhardness and thickness of formed layer of experimental materials Al99-5. By increasing of electrolyte temperature, the values of layer microhardness and thickness layer increase, namely about 0.78 % at the increasing of electrolyte temperature by 1 °C. By lengthening of anodizing time grows the value of layer thickness, but only to the value of the critical deposition time, when chemical dissolution of the layer start to be more prominent. By voltage increasing, values of layer thickness and micro-hardness are increased in the range of the used experimental values.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CI - Průmyslová chemie a chemické inženýrství

OECD FORD obor

—

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metalurgija

ISSN

0543-5846

e-ISSN

—

Svazek periodika

roč. 55

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

HR - Chorvatská republika

Počet stran výsledku

4

Strana od-do

799-802

Kód UT WoS článku

000376167100059

EID výsledku v databázi Scopus

—