Usage of Initial surface absorption method for evaluation of degradation of concrete exposed to high temperatures Usage of Initial surface absorption method for evaluation of degradation of concrete
The high temperatures have negative influence on concrete constructions in term of failure of inner concrete structure. The rate of permeability of surface layer. Theexplosive spalling could occur if the rate of permeability of ...
JN - Stavebnictví
- 2014 •
- O
Rok uplatnění
O - Ostatní výsledky
Device for the ozon degradation measurements
The output is device allowing measurements of ozone heterogeneous degradation at various surfaces in temperature dependence....
BL - Fyzika plasmatu a výboje v plynech
- 2013 •
- Gfunk
Rok uplatnění
Gfunk - Funkční vzorek
Effect of temperature on the microstructure glass molds
In this paper I will focus on low-alloy cast-iron glass molds, which occur in the production process to degrade the surface of contact with the enamel, making the product creates a visual defect and form must be changed, as reflecte...
JK - Koroze a povrchové úpravy materiálu
- 2009 •
- D
Rok uplatnění
D - Stať ve sborníku
Comparing Measured and Computed Surface Temperatures of Saint Vitus Cathedral Bearing System
of temperatures are one of the effects which cause degradation of the structure. Tendency to understand of this degradation process leads to measurement of surface temperatures of structure surface
JN - Stavebnictví
- 2008 •
- D
Rok uplatnění
D - Stať ve sborníku
Degradation of protective effect of surface layer on Ni3Al-Cr in hydrogen environment.
that the addition of Cr degrades the - otherwise very good - high-temperature protective abilityProtective effect of surface layer on Cr-doped (4 and 8 at. % Cr) Ni3Al intermetallic was studied by high-temperature...
BM - Fyzika pevných látek a magnetismus
- 2001 •
- D
Rok uplatnění
D - Stať ve sborníku
Heat treatment technology for parts produced by 3D additive SLM technology from titanium alloys without surface degradation due to oxidation at high temperatures
without surface degradation due to oxidation at high temperatures, including the plate and supports for the given part. The heat treatment took place in a high-temperature without surface degradation<...
Thermodynamics
- 2024 •
- Ztech
Rok uplatnění
Ztech - Ověřená technologie
Structure of Injection-Molded Beta-Polypropylene and Research Perspectives of Its Degradability
. Furthermore, the level of surface damage caused by degradation strongly depends and their degradability were studied using X-ray diffractometry and light microscopy. It was found that the mold temperature signifi...
CD - Makromolekulární chemie
- 2003 •
- D
Rok uplatnění
D - Stať ve sborníku
Rights ways of application for external wooden elements
effect when elements are exposed to sunshine can lead onto the surface degradationThe climate - mostly the temperature and water - represents a wide range into the building and its wooden structures. Humidity and tempe...
JN - Stavebnictví
- 2006 •
- D
Rok uplatnění
D - Stať ve sborníku
Devices for the temperature dependence measurement of the ozone heterogeneous decomposition
The constructed device is used to measure the ozone decomposition on internal surfaces of pipes at atmospheric pressure in the temperature dependence....
BL - Fyzika plasmatu a výboje v plynech
- 2016 •
- Gfunk •
- Odkaz
Rok uplatnění
Gfunk - Funkční vzorek
Výsledek na webu
Analysis of Influences Causing Surface Degradation on Objects with ETICS
The paper describes the piece of knowledge about emissivity effecting the moisture saturation of building materials in a surface layer and results of modeling of non-stationary temperature and moisture process in a cladding of build...
JN - Stavebnictví
- 2006 •
- Jx
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
- 1 - 10 z 130 437