Mikromechanisms of fatigue crack propagation under shear modes in austenitic steel
of the stress intensity factor range and the near-threshold crack growth rates under shear loading modes II and III. Fatigue cracks under shear mode II were kinked while those under shear mode II...
JL - Únava materiálu a lomová mechanika
- 2010 •
- D
Rok uplatnění
D - Stať ve sborníku
Quantitative Fractography of Fatigue Long Crack Growth under Remote Shear Loading Modes
Quantitative Fractography of Fatigue Long Crack Growth under Remote Shear Loading Modes...
JL - Únava materiálu a lomová mechanika
- 2008 •
- D
Rok uplatnění
D - Stať ve sborníku
Three-dimensional morphology of fracture surfaces generated by mode II and III fatigue loading in ferrite and austenite.
This work is focused on an experimental study of shear-mode crack propagation with respect to the remote shear direction. The tendency to mode I crack branching is found. Three experimental setups are used for a ge...
JL - Únava materiálu a lomová mechanika
- 2013 •
- Jx •
- Odkaz
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
Výsledek na webu
Shear Fracture - Testing Configuration for Cement Paste in Mode II
This article is focused on different ways of testing in mode II. There are presented three basic modes of a shear. The best way how to test the fracture mode II and determinate the critical factor KII of cement pas...
JN - Stavebnictví
- 2016 •
- O
Rok uplatnění
O - Ostatní výsledky
Bi-material notches under various normal-shear loading modes
on the assumptions of the prevailing normal mode of loading. However, in engineering practice there are cases of loading and failure close to the shear mode of loading. The aim of the work to a combination of normal and
Audio engineering, reliability analysis
- 2014 •
- Jimp •
- Odkaz
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
Bi-material notches under various normal-shear loading modes
on the assumptions of the prevailing normal mode of loading. However, in engineering practice there are cases of loading and failure close to the shear mode of loading. The aim of the work to a combination of normal and
JL - Únava materiálu a lomová mechanika
- 2014 •
- D
Rok uplatnění
D - Stať ve sborníku
Modelling of Tortuous Crack Fronts in Shear Loading Mode
under shear modes II, III and II+III in bcc metals. Cylindrical bars with circumferential cracked notch were loaded by shear force. The notch is located in the cross-section where no bending moment is present and it is loa...
Audio engineering, reliability analysis
- 2017 •
- O
Rok uplatnění
O - Ostatní výsledky
Influence of Secondary Phase on Intrinsic Threshold and Path of Shear-Mode Fatigue Cracks in Metals
the local shear and the local opening growth mode. Unlike in the case of opening mode I of the shear-mode cracks in dependence of the type of the secondary phase. The cementite the local shear an...
Materials engineering
- 2018 •
- Jimp •
- Odkaz
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
Transition from the saltation mode of bed load transport to the rolling mode
of sediment transport incipient motion of the bed load particles the shear stress for the transition process from saltation mode to rolling mode can be defined. The shear stress numerical solution reveals that the...
BK - Mechanika tekutin
- 2009 •
- D
Rok uplatnění
D - Stať ve sborníku
Experimental Investigation of Modes II and III Fatigue Crack Growth in Unalloyed Titanium
bars with a circumferential cracked notch loaded in shear (modes II, III and II + III) and torsion (mode III). Fractography analysis showed that the crack growthThe study is focused on finding and describing microscopic pa...
Audio engineering, reliability analysis
- 2014 •
- Jimp •
- Odkaz
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
- 1 - 10 z 26 098