Microstructure and properties of martensitic precipitation-hardening steel MLX 17 after long-term ageing at 475 °C
by embrittlement at 475 °C induced by decomposition of the microstructure into two arranged, microstructure and substructure. Therefore, the ageing at 475 °C for 1,000, 2,000 and 3,000. Ageing at 475<...
Materials engineering
- 2018 •
- D •
- Odkaz
Rok uplatnění
D - Stať ve sborníku
Výsledek na webu
EFFECT OF LONG-TERM AGEING AT 475 °C ON PROPERTIES AND MICROSTRUCTURE OF CUSTOM 465 STEEL
arranged solid solutions α+α´ (embrittlement at 475 °C) or by precipitation of chromium at 475 °C) on the material properties, microstructure and substructure energy was detected after ageing at 475
Materials engineering
- 2017 •
- D •
- Odkaz
Rok uplatnění
D - Stať ve sborníku
Výsledek na webu
The Effect of Long-Term Ageing at 475 °C on Microstructure and Properties of a Precipitation Hardening MartensiticStainless Steel
The effect of long-term ageing (1000, 2000, and 3000 h) at 475 °C on mechanical with time of ageing at 475 °C. Ageing resulted in a gradual slight decline (up to 10 austenite during long-term ageing at 475...
Materials engineering
- 2022 •
- Jimp •
- Odkaz
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
EFFECT OF LONG-TERM AGEING AT 475 oC ON PROPERTIES AND MICROSTRUCTURE OF CUSTOM 465 STEEL
arranged solid solutions α+α' (embrittlement at 475 oC) or by precipitationThe steels with high chromium content are known to suffer embrittlement materials having chromium content close to the minimum embrittleme...
Materials engineering
- 2017 •
- D •
- Odkaz
Rok uplatnění
D - Stať ve sborníku
Výsledek na webu
Decomposition and Precipitation Process During Thermo-mechanical Fatigue of Duplex Stainless Steel
The so-called 748 K (475 °C) embrittlement is one of the main drawbacks for the application of ferritic-austenitic duplex stainless steels (DSS) at higher temperatures tests performed on a DSS in the temperature range betwe...
JL - Únava materiálu a lomová mechanika
- 2016 •
- Jx •
- Odkaz
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
Výsledek na webu
The Hydrogen Embrittlement of C-Mn Steels
Evaluation of susceptibility of C-Mn steels to hydrogen embrittlement were studied in this paper. Tensile tests performed on previously electrolytically charged specimens were used in this work. The specimens were taken in three dec...
JG - Hutnictví, kovové materiály
- 2002 •
- D
Rok uplatnění
D - Stať ve sborníku
EVOLUTION OF MICROSTRUCTURE AND EMBRITTLEMENT DURING THE TEMPERING PROCESS IN SiCrCu MEDIUM C STEELS
The effect of Cu and Si contents on the evolution of embrittlement during 200-500 degrees C was investigated in medium-carbon steels with 0.48 w/% and 0.57 w/% of C. The results showed that the higher silicon content shifte...
Materials engineering
- 2023 •
- Jimp •
- Odkaz
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
Hydrogen embrittlement of tantalum and tantalum coatings
temperatures (30 °C, 80 °C and 150 °C). The goal of the experiment was to test the impact of hydrogen embrittlement of a material surface on its overall corrosion resistance. It is assumed that hydrogen embrit...
JK - Koroze a povrchové úpravy materiálu
- 2012 •
- Jx
Rok uplatnění
Jx - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
Behavior of the Steel T91 under Multi Axial Loading in Contact with Liquid and Solid Pb
close to the melting point of Pb, the steel is sensitive to LME (350-400 °C) and to Solid Metal Induced Embrittlement (SMIE) (300 °C). The cracking was stimulatedIn this work, the conditions for the occurrence of Liquid Me...
Materials engineering
- 2017 •
- Jimp •
- Odkaz
Rok uplatnění
Jimp - Článek v periodiku v databázi Web of Science
Výsledek na webu
Behavior of the steel T91 under multi axial loading in contact with liquid and solid Pb
close to the melting point of Pb, the steel is sensitive to LME (350-400 degrees C) and to Solid Metal Induced Embrittlement (SMIE) (300 degrees C). The crackingIn this work, the conditions for the occurrence of Liquid Met...