An influence of thermal treatment on mechanical properties of FeNiB amorphous alloys
Original language description
An influence of thermal treatment in the temperature range of 150 - 350 °C on the structural and mechanical properties of an amorphous FeNiB alloy is investigated. The high tensile strength of 2200 MPa in the as-prepared amorphous state slightly decreases with increasing temperature of annealing up to approximately 200 °C in opposite to microhardness where an increase is observed. Above 200 °C a pronounced deterioration of both characteristics reflect the embrittlement of amorphous structure without anyindications of crystallization.
Czech name
Vliv tepelného namáhání na mechanické vlastnosti FeNiB amorfní slitiny
Czech description
Vliv tepelného namáhání v teplotním intervalu 150 - 350 °C na změny struktury a mechanických vlastností je studován na vzorcích FeNiB s amorfní strukturou. Vysoká pevnost v tahu, 2200 MPa, naměřená u vzorku v původním amorfním stavu mírně klesá s rostoucí teplotou žíhání vzorků do přibližně 200 °C na rozdíl od mikrotvrdosti, u níž je pozorován růst. Nad touto teplotou však dochází k výraznému zhoršení obou vlastností vlivem křehnutí amorfní struktury bez jakýchkoliv známek krystalizace.