An Influence of thermal treatment on the mechanical properties of FeNiB amorphous alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00098667" target="_blank" >RIV/68081723:_____/05:00098667 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
An Influence of thermal treatment on the mechanical properties of FeNiB amorphous alloy
Original language description
An influence of thermal treatment in the temperature range 150 - 350 °C on the structural and mechanical properties of an amorphous FeNiB alloy is investigated. The high tensile strength of 2200 MPa in the as-prepared amorphous state slightly decreases with increasing annealing temperature up to approximately 200 °C in opposite to microhardness where an increase is observed. Above 200 °C a pronounced deterioration of both characteristics is observed which reflects the embrittlement of amorphous structure without any indication of crystallization.
Czech name
Vliv tepelného zpracování na mechanické vlastnosti slitiny FeNiB
Czech description
Byl studován vliv tepelného zpracování v rozsahu 150 - 350 °C na strukturní a mechanické vlastnosti amorfní slitiny na bázi FeNiB. Byla zjištěna vysoká mez pevnosti 2200 Mpa v původním stavu, která se vzrůstající teplotou přibližně do 200 °C klesala, oproti stoupajícím hodnotám mikrotvrdosti. Nad 200°C se obě charakteristiky významně zhoršují, což odráží výrazné zkřehnutí amorfní struktury. Nebyly pozorovány žádné známky krystalizace.