Cyclic-oxidation resistance of protective silicide layers on titanium
Original language description
Influence of the powder siliconization and gas nitridation on the improvement of the titanium resistance against oxidation. After coating the surface with the silicon the samples were annealed at 900-11000C so that titanium oxide and nitride layers werecreated
Czech name
Odolnost ochranných silicidových vrstev na titanu proti cyclické oxidaci
Czech description
byl studován vliv nitridace a práškového křemíkování na zvýšení odolnosti titanu proti oxidaci. Po nanesení křemíku na povrch byly vzorky žíhány při 900-11000C čímž se vytvořily vrystvy titanových oxudů a nitridů

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
<a href="/en/project/IAA1010414" target="_blank" >IAA1010414: Crystallization of single- and multiphase materials</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)