Charakterizace povrchových úprav kachlů a reliéfů z hradčanských paláců a identifikace zdrojů poškození glazur

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00023281%3A_____%2F19%3AN0000016" target="_blank" >RIV/00023281:_____/19:N0000016 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/67985912:_____/19:00510406 RIV/60461373:22310/19:43918344

Výsledek na webu

<a href="https://mck.technicalmuseum.cz/wp-content/uploads/2017/10/CHARAKTERIZACE-POVRCHOV%C3%9DCH-%C3%9APRAV-KACHL%C5%AE-A-RELI%C3%89F%C5%AE-Z-HRAD%C4%8CANSK%C3%9DCH-PAL%C3%81C%C5%AE-A-IDENTIFIKACE-ZDROJ%C5%AE-PO%C5%A0KOZEN%C3%8D-GLAZUR.pdf" target="_blank" >https://mck.technicalmuseum.cz/wp-content/uploads/2017/10/CHARAKTERIZACE-POVRCHOV%C3%9DCH-%C3%9APRAV-KACHL%C5%AE-A-RELI%C3%89F%C5%AE-Z-HRAD%C4%8CANSK%C3%9DCH-PAL%C3%81C%C5%AE-A-IDENTIFIKACE-ZDROJ%C5%AE-PO%C5%A0KOZEN%C3%8D-GLAZUR.pdf</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

čeština

Název v původním jazyce

Charakterizace povrchových úprav kachlů a reliéfů z hradčanských paláců a identifikace zdrojů poškození glazur

Popis výsledku v původním jazyce

Mezi archeologickými nálezy hradčanských paláců jsou zastoupeny různé typy kamnářských kachlů a unikátní velkoformátové reliéfy s výraznými barevnými dekory. Povrchové úpravy těchto keramických výrobků vykazují různé typy poškození. Hlavním cílem příspěvku je uvést základní charakterizaci střepových hmot a glazur vybraných kachlů včetně barvících složek. K určení chemického a mineralogického složení byly použity kombinace metod mikroskopických (OM, SEM) a rentgenových analýz (XRF, pXRF, XRD) a Ramanovy spektroskopie (RS). Termické analýzy (DIL) byly využity k identifikaci zdrojů defektů poškozených povrchů. Olovnaté glazury některých kamnářských kachlů vykazovaly výrazné popraskání. Bylo prokázáno, že jejich hlavním zdrojem bylo tahové pnutí v povrchové vrstvě vytvořené při výrobě. Nesoulad koeficientů teplotní roztažnosti byl prohlouben působením vlhkosti při uložení části kachlů v odpadních jímkách.

Název v anglickém jazyce

Characterization of surface finishing of tiles from Hradčany Palaces and identification of glaze defects sources

Popis výsledku anglicky

Various types of stove tiles and unique large-format tiles with relief colourful decors are represented among the archaeological finds from Hradčany Palaces. Surface finishing of these ceramic products is degraded by different types of defects. The aim of this paper is to present the basic characterization of ceramic bodies and glazes of selected tile fragments including the identification of colouring agents. A combination of microscopic (OM, SEM) and X-ray (XRF, pXRF, XRD) analyses or Raman spectroscopy (RS) was used to determine chemical and mineralogical compositions. Thermal analyses (especially DIL) were used to identify possible sources of defects of degraded surfaces. Severe crazing and cracking were found on surfaces of lead glazes of some stove tiles. It was proved that the main source of crazing was tensile stress within glazes developed during production. The mismatch of the coefficients of thermal expansion was exceeded by the effect of moisture expansion of ceramic bodies during deposition in the waste pit.

Druh

J_ost - Ostatní články v recenzovaných periodicích

CEP obor

—

OECD FORD obor

60401 - Arts, Art history

Projekt

<a href="/cs/project/DG18P02OVV028" target="_blank" >DG18P02OVV028: Technologie ošetření a identifikace degradačních procesů keramických nálezů z hradčanských paláců - Metody restaurování a konzervování pórovité i slinuté keramiky a porcelánu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Fórum pro konzervátory-restaurátory

ISSN

1805-0050

e-ISSN

2571-4384

Svazek periodika

2019, 9

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

10

Strana od-do

116-125

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—