Bisphenol A Release from Dental Composites and Resin-Modified Glass Ionomers under Two Polymerization Conditions
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00023761%3A_____%2F22%3AN0000011" target="_blank" >RIV/00023761:_____/22:N0000011 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/60461373:22330/22:43925488 RIV/00064165:_____/22:10435425 RIV/00216208:11110/22:10435425
Výsledek na webu
<a href="https://www.mdpi.com/2073-4360/14/1/46" target="_blank" >https://www.mdpi.com/2073-4360/14/1/46</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/polym14010046" target="_blank" >10.3390/polym14010046</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Bisphenol A Release from Dental Composites and Resin-Modified Glass Ionomers under Two Polymerization Conditions
Popis výsledku v původním jazyce
Bisphenol A (BPA)-based monomers are commonly contained in dental resin-based materials. As BPA is an endocrine disruptor, its long-term release from restorative composites and resin-modified glass ionomers (RM-GICs) under two polymerization conditions was measured in this study. Specimens of two conventional composites containing BPA-based monomers, two "BPA-free" composites, and two RM-GICs were polymerized from one side for 20 s at 1300 mW/cm(2) or for 5 s at 3000 mW/cm(2). The amounts of BPA released in artificial saliva and methanol after 1, 4, 9, 16, 35, 65, 130, and 260 days were measured using liquid chromatography-tandem mass spectrometry. The highest amounts of BPA were released from conventional composites, followed by RM-GICs, while the least was released from "BPA-free" composites. Amounts of released BPA were significantly higher in methanol and decreased gradually after the first day. Fast polymerization (5 s at 3000 mW/cm(2)) resulted in a significantly higher release of BPA after 1 day, but the effect of polymerization conditions was not significant overall. In conclusion, fast polymerization increased the initial release of BPA, but the released amounts were significantly lower than the current tolerable daily intake (4 mu g/kg body weight/day) even in methanol, representing the worst-case scenario of BPA release.
Název v anglickém jazyce
Bisphenol A Release from Dental Composites and Resin-Modified Glass Ionomers under Two Polymerization Conditions
Popis výsledku anglicky
Bisphenol A (BPA)-based monomers are commonly contained in dental resin-based materials. As BPA is an endocrine disruptor, its long-term release from restorative composites and resin-modified glass ionomers (RM-GICs) under two polymerization conditions was measured in this study. Specimens of two conventional composites containing BPA-based monomers, two "BPA-free" composites, and two RM-GICs were polymerized from one side for 20 s at 1300 mW/cm(2) or for 5 s at 3000 mW/cm(2). The amounts of BPA released in artificial saliva and methanol after 1, 4, 9, 16, 35, 65, 130, and 260 days were measured using liquid chromatography-tandem mass spectrometry. The highest amounts of BPA were released from conventional composites, followed by RM-GICs, while the least was released from "BPA-free" composites. Amounts of released BPA were significantly higher in methanol and decreased gradually after the first day. Fast polymerization (5 s at 3000 mW/cm(2)) resulted in a significantly higher release of BPA after 1 day, but the effect of polymerization conditions was not significant overall. In conclusion, fast polymerization increased the initial release of BPA, but the released amounts were significantly lower than the current tolerable daily intake (4 mu g/kg body weight/day) even in methanol, representing the worst-case scenario of BPA release.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10404 - Polymer science
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Polymers
ISSN
2073-4360
e-ISSN
2073-4360
Svazek periodika
14
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
14
Strana od-do
Article Number 46
Kód UT WoS článku
000751393000001
EID výsledku v databázi Scopus
2-s2.0-85121826475