Chemical polishing of CdTe and CdZnTe in iodine-methanol etching solutions

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10106112" target="_blank" >RIV/00216208:11320/11:10106112 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.springerlink.com/content/87417434v1552n2w/" target="_blank" >http://www.springerlink.com/content/87417434v1552n2w/</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s11664-011-1649-2" target="_blank" >10.1007/s11664-011-1649-2</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Chemical polishing of CdTe and CdZnTe in iodine-methanol etching solutions

Popis výsledku v původním jazyce

Iodine-containing polishing etchants were tested on CdTe and CdZnTe surfaces with different orientations. The nature of the chemical dissolution of CdTe with (111)A, (111)B, (110), and (100) orientations in the I2-methanol solution was studied. It was established that this dissolution is diffusion controlled. The study of the chemical composition and structure of the (211)B CdZnTe surfaces etched under different conditions was carried out. X-ray photoelectron spectroscopy (XPS) measurements showed thata stoichiometric surface was achieved after short heating of the etched surface in vacuum.

Název v anglickém jazyce

Chemical polishing of CdTe and CdZnTe in iodine-methanol etching solutions

Popis výsledku anglicky

Iodine-containing polishing etchants were tested on CdTe and CdZnTe surfaces with different orientations. The nature of the chemical dissolution of CdTe with (111)A, (111)B, (110), and (100) orientations in the I2-methanol solution was studied. It was established that this dissolution is diffusion controlled. The study of the chemical composition and structure of the (211)B CdZnTe surfaces etched under different conditions was carried out. X-ray photoelectron spectroscopy (XPS) measurements showed thata stoichiometric surface was achieved after short heating of the etched surface in vacuum.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Electronic Materials

ISSN

0361-5235

e-ISSN

—

Svazek periodika

40

Číslo periodika v rámci svazku

8

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

7

Strana od-do

1802-1808

Kód UT WoS článku

000292466000032

EID výsledku v databázi Scopus

—