Stress Relaxation in an AZ31 Magnesium alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10108508" target="_blank" >RIV/00216208:11320/11:10108508 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.465.101" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.465.101</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.465.101" target="_blank" >10.4028/www.scientific.net/KEM.465.101</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Stress Relaxation in an AZ31 Magnesium alloy
Popis výsledku v původním jazyce
Stress relaxation tests have been used in order to determine parameters of a possible thermally activated process in AZ31 magnesium alloy. The samples were deformed at a constant initial strain rate of 6.7x10(-5) s(-1) various temperatures between room temperature and 300 degrees C. Stress relaxation, i.e. a decrease in the stress with time, was measured at various stress levels and at various temperatures. An analysis of the stress relaxation curves enabled to estimate the internal stress as a functionof the strain and the test temperature. It has been shown that the activation volume is a function of the effective stress independently of the deformation temperature.
Název v anglickém jazyce
Stress Relaxation in an AZ31 Magnesium alloy
Popis výsledku anglicky
Stress relaxation tests have been used in order to determine parameters of a possible thermally activated process in AZ31 magnesium alloy. The samples were deformed at a constant initial strain rate of 6.7x10(-5) s(-1) various temperatures between room temperature and 300 degrees C. Stress relaxation, i.e. a decrease in the stress with time, was measured at various stress levels and at various temperatures. An analysis of the stress relaxation curves enabled to estimate the internal stress as a functionof the strain and the test temperature. It has been shown that the activation volume is a function of the effective stress independently of the deformation temperature.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/IAA201120902" target="_blank" >IAA201120902: Odpevňovací procesy v průběhu deformace hořčíkové slitiny AZ31</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials
ISSN
1013-9826
e-ISSN
—
Svazek periodika
465
Číslo periodika v rámci svazku
—
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
4
Strana od-do
101-104
Kód UT WoS článku
000291704700020
EID výsledku v databázi Scopus
—