Origin of high-coercivity in nanocomposites by single-precursor sol-gel method
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F11%3A10118940" target="_blank" >RIV/00216208:11320/11:10118940 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11310/11:10118940
Výsledek na webu
<a href="http://iopscience.iop.org/1742-6596/266/1/012123" target="_blank" >http://iopscience.iop.org/1742-6596/266/1/012123</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1742-6596/266/1/012123" target="_blank" >10.1088/1742-6596/266/1/012123</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Origin of high-coercivity in nanocomposites by single-precursor sol-gel method
Popis výsledku v původním jazyce
We have fabricated high-coercivity nanocomposites constituted of Fe2O3 or CoFe2O4 nanocrystals embedded in amorphous silica matrix by a single-molecule precursor sol-gel method. Our approach enables smooth variation of the Fe(Co) : Si ratio up to 40 weight % of the magnetic phase, resulting in high density nanocomposite. Final crystallite size and phase composition was adjusted by subsequent heat treatment. The Fe2O3/SiO2 samples annealed at 1000 and 1100 degrees C revealed coercivity, H-c similar to 2T at 300 K due to formation of the metastable epsilon-Fe2O3 phase. The CoFe2O4/SiO2 composites exhibit enhancement of the H-c value with increasing annealing temperature. Origin of the large coercivity in the two types of the magnetically hard nanocomposites will be discussed.
Název v anglickém jazyce
Origin of high-coercivity in nanocomposites by single-precursor sol-gel method
Popis výsledku anglicky
We have fabricated high-coercivity nanocomposites constituted of Fe2O3 or CoFe2O4 nanocrystals embedded in amorphous silica matrix by a single-molecule precursor sol-gel method. Our approach enables smooth variation of the Fe(Co) : Si ratio up to 40 weight % of the magnetic phase, resulting in high density nanocomposite. Final crystallite size and phase composition was adjusted by subsequent heat treatment. The Fe2O3/SiO2 samples annealed at 1000 and 1100 degrees C revealed coercivity, H-c similar to 2T at 300 K due to formation of the metastable epsilon-Fe2O3 phase. The CoFe2O4/SiO2 composites exhibit enhancement of the H-c value with increasing annealing temperature. Origin of the large coercivity in the two types of the magnetically hard nanocomposites will be discussed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GP202%2F08%2FP006" target="_blank" >GP202/08/P006: Nanodimenzionální uspořádání v přechodných kovech a jejich sloučeninách</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Physics: Conference Series
ISSN
1742-6588
e-ISSN
—
Svazek periodika
266
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
5
Strana od-do
1-5
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—