The Effect of Reversed Loading Conditions on the Mechanical Behaviour of Extruded Magnesium Alloy AZ31

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F12%3A10129207" target="_blank" >RIV/00216208:11320/12:10129207 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The Effect of Reversed Loading Conditions on the Mechanical Behaviour of Extruded Magnesium Alloy AZ31

Popis výsledku v původním jazyce

An indirectly extruded round bar of magnesium alloy AZ31 has been subjected to a cyclic test consisting of preloading in compression to different values of maximum stress followed by a single tensile test segment. Concurrent acoustic emission measurements were used to determine the active deformation mechanisms during plastic flow and work hardening. Electron backscattering diffraction was applied to obtain local orientation images in order to reveal twins and twinned fractions of the microstructure. Twins form preferentially in larger grains during the compression test segment and only with increasing stress do smaller grains show twinning. Some grains are completely re-oriented as a result of twinning. During the tensile test segment, untwinning is the most significant deformation mechanism although in some re-oriented grains new twins also nucleate. The acoustic emission count rates confirm that this is only the case after compression to higher stress levels.

Název v anglickém jazyce

The Effect of Reversed Loading Conditions on the Mechanical Behaviour of Extruded Magnesium Alloy AZ31

Popis výsledku anglicky

An indirectly extruded round bar of magnesium alloy AZ31 has been subjected to a cyclic test consisting of preloading in compression to different values of maximum stress followed by a single tensile test segment. Concurrent acoustic emission measurements were used to determine the active deformation mechanisms during plastic flow and work hardening. Electron backscattering diffraction was applied to obtain local orientation images in order to reveal twins and twinned fractions of the microstructure. Twins form preferentially in larger grains during the compression test segment and only with increasing stress do smaller grains show twinning. Some grains are completely re-oriented as a result of twinning. During the tensile test segment, untwinning is the most significant deformation mechanism although in some re-oriented grains new twins also nucleate. The acoustic emission count rates confirm that this is only the case after compression to higher stress levels.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GPP108%2F10%2FP430" target="_blank" >GPP108/10/P430: Studium deformačních mechanismů v nových hořčíkových slitin při jednoosém a nízko cyklovém namáhaní metodou akustické emise</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Physica Polonica A

ISSN

0587-4246

e-ISSN

—

Svazek periodika

122

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

444-449

Kód UT WoS článku

000309019200006

EID výsledku v databázi Scopus

—