On the Effect of the Extrusion Speed on Microstructure and Plastic Deformation of ZE10 and ZEK100 Magnesium Alloys - an Acoustic Emission Study

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F12%3A10130331" target="_blank" >RIV/00216208:11320/12:10130331 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

On the Effect of the Extrusion Speed on Microstructure and Plastic Deformation of ZE10 and ZEK100 Magnesium Alloys - an Acoustic Emission Study

Popis výsledku v původním jazyce

Mg-Zn-based alloys ZE10 and ZEK100 have been extruded at different speeds varying from 1 m/min to 20 m/min. Specimens taken in the extrusion direction were uniaxially loaded in tension and compression at room temperature. The results are discussed usingconcurrent acoustic emission monitoring during mechanical testing and the acoustic emission signal analysis that correlates the microstructure and the stress-strain curves to the possible deformation mechanisms. In all tests, the acoustic emission response exhibited a large acoustic emission peak at the beginning of plastic deformation. A small local maximum on the onset of the acoustic emission activity was frequently observed, i.e. at very low stresses. For the alloys with bimodal grain structure tested in compression, an additional acoustic emission peak appeared at larger strains. This peculiar behavior can be explained by interplay of (10-12)-twinning and dislocation slip in samples with various grain size distributions.

Název v anglickém jazyce

On the Effect of the Extrusion Speed on Microstructure and Plastic Deformation of ZE10 and ZEK100 Magnesium Alloys - an Acoustic Emission Study

Popis výsledku anglicky

Mg-Zn-based alloys ZE10 and ZEK100 have been extruded at different speeds varying from 1 m/min to 20 m/min. Specimens taken in the extrusion direction were uniaxially loaded in tension and compression at room temperature. The results are discussed usingconcurrent acoustic emission monitoring during mechanical testing and the acoustic emission signal analysis that correlates the microstructure and the stress-strain curves to the possible deformation mechanisms. In all tests, the acoustic emission response exhibited a large acoustic emission peak at the beginning of plastic deformation. A small local maximum on the onset of the acoustic emission activity was frequently observed, i.e. at very low stresses. For the alloys with bimodal grain structure tested in compression, an additional acoustic emission peak appeared at larger strains. This peculiar behavior can be explained by interplay of (10-12)-twinning and dislocation slip in samples with various grain size distributions.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Physica Polonica A

ISSN

0587-4246

e-ISSN

—

Svazek periodika

122

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

4

Strana od-do

593-596

Kód UT WoS článku

000309019200042

EID výsledku v databázi Scopus

—