Vacancy-induced hardening in Fe-Al alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F13%3A10189486" target="_blank" >RIV/00216208:11320/13:10189486 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1088/1742-6596/443/1/012025" target="_blank" >http://dx.doi.org/10.1088/1742-6596/443/1/012025</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1742-6596/443/1/012025" target="_blank" >10.1088/1742-6596/443/1/012025</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Vacancy-induced hardening in Fe-Al alloys
Popis výsledku v původním jazyce
Hardness of Fe-Al alloys shows a non-trivial dependence on chemical composition and thermal treatment of samples and cannot be fully explained by consideration of intermetallic phases formed according to the equilibrium phase diagram of Fe-Al system. Hardening in Fe-Al alloys caused by quenched-in non-equilibrium vacancies was studied in this work. Non-equilibrium vacancies introduced into the alloys by quenching from 1000 degrees C were detected by means of positron annihilation spectroscopy. The concentration of quenched-in vacancies was found to strongly increase with increasing Al content from approximate to 10(-5) at.(-1) in the alloy with c(Al) = 18 at. % up to approximate to 10(-1) at.(-1) in the alloy with c(Al) = 45 at. %. Comparison of the vacancy concentration and the Vickers microhardness revealed that hardening is proportional to square root of concentration of quenched-in vacancies.
Název v anglickém jazyce
Vacancy-induced hardening in Fe-Al alloys
Popis výsledku anglicky
Hardness of Fe-Al alloys shows a non-trivial dependence on chemical composition and thermal treatment of samples and cannot be fully explained by consideration of intermetallic phases formed according to the equilibrium phase diagram of Fe-Al system. Hardening in Fe-Al alloys caused by quenched-in non-equilibrium vacancies was studied in this work. Non-equilibrium vacancies introduced into the alloys by quenching from 1000 degrees C were detected by means of positron annihilation spectroscopy. The concentration of quenched-in vacancies was found to strongly increase with increasing Al content from approximate to 10(-5) at.(-1) in the alloy with c(Al) = 18 at. % up to approximate to 10(-1) at.(-1) in the alloy with c(Al) = 45 at. %. Comparison of the vacancy concentration and the Vickers microhardness revealed that hardening is proportional to square root of concentration of quenched-in vacancies.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Journal of Physics: Conference Series
ISBN
—
ISSN
1742-6588
e-ISSN
—
Počet stran výsledku
4
Strana od-do
—
Název nakladatele
IOP PUBLISHING LTD
Místo vydání
BRISTOL
Místo konání akce
Bristol
Datum konání akce
19. 8. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000321739400025