Vacancy-induced hardening in Fe-Al alloys
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00421498" target="_blank" >RIV/68081723:_____/13:00421498 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1088/1742-6596/443/1/012025" target="_blank" >http://dx.doi.org/10.1088/1742-6596/443/1/012025</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1742-6596/443/1/012025" target="_blank" >10.1088/1742-6596/443/1/012025</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Vacancy-induced hardening in Fe-Al alloys
Popis výsledku v původním jazyce
Hardness of Fe-Al alloys shows a non-trivial dependence on chemical composition and thermal treatment of samples and cannot be fully explained by consideration of intermetallic phases formed according to the equilibrium phase diagram of Fe-Al system. Hardening in Fe- Al alloys caused by quenched-in non-equilibrium vacancies was studied in this work. Non- equilibrium vacancies introduced into the alloys by quenching from 1000 C were detected by means of positron annihilation spectroscopy. The concentration of quenched-in vacancies was found to strongly increase with increasing Al content from 105 at.1 in the alloy with cAl = 18 at. % up to 101 at.1 in the alloy with cAl = 45 at. %. Comparison of the vacancy concentration and the Vickers microhardness revealed that hardening is proportional to square root of concentration of quenched-in vacancies.
Název v anglickém jazyce
Vacancy-induced hardening in Fe-Al alloys
Popis výsledku anglicky
Hardness of Fe-Al alloys shows a non-trivial dependence on chemical composition and thermal treatment of samples and cannot be fully explained by consideration of intermetallic phases formed according to the equilibrium phase diagram of Fe-Al system. Hardening in Fe- Al alloys caused by quenched-in non-equilibrium vacancies was studied in this work. Non- equilibrium vacancies introduced into the alloys by quenching from 1000 C were detected by means of positron annihilation spectroscopy. The concentration of quenched-in vacancies was found to strongly increase with increasing Al content from 105 at.1 in the alloy with cAl = 18 at. % up to 101 at.1 in the alloy with cAl = 45 at. %. Comparison of the vacancy concentration and the Vickers microhardness revealed that hardening is proportional to square root of concentration of quenched-in vacancies.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP108%2F11%2F1350" target="_blank" >GAP108/11/1350: Vlivy jádra a povrchu nanozrn na strukturní a fyzikální vlastnosti materiálů na bázi železa připravených mletim a mechanickým legováním.</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Physics: Conference Series
ISSN
1742-6588
e-ISSN
—
Svazek periodika
443
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
4
Strana od-do
012025
Kód UT WoS článku
000321739400025
EID výsledku v databázi Scopus
—