Helium behavior in ferritic/martensitic steels irradiated in spallation target

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F15%3A10316039" target="_blank" >RIV/00216208:11320/15:10316039 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jnucmat.2014.10.014" target="_blank" >http://dx.doi.org/10.1016/j.jnucmat.2014.10.014</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jnucmat.2014.10.014" target="_blank" >10.1016/j.jnucmat.2014.10.014</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Helium behavior in ferritic/martensitic steels irradiated in spallation target
Popis výsledku v původním jazyce
Two positron annihilation spectroscopy (PAS) techniques have been used for the investigation of helium behavior in STIP samples. Positron lifetime measurements and coincidence Doppler broadening spectroscopy have been employed together in a complex PAS characterization of RAFM steel irradiated in a mixed neutron-proton spectrum up to 20 dpa and 1800 appm He. Both techniques show an increase of the He-to-dpa ratio up to similar to 10 dpa. At higher irradiation loads, the ratio is decreasing, which was attributed to the formation and growth of helium bubbles.
Název v anglickém jazyce
Helium behavior in ferritic/martensitic steels irradiated in spallation target
Popis výsledku anglicky
Two positron annihilation spectroscopy (PAS) techniques have been used for the investigation of helium behavior in STIP samples. Positron lifetime measurements and coincidence Doppler broadening spectroscopy have been employed together in a complex PAS characterization of RAFM steel irradiated in a mixed neutron-proton spectrum up to 20 dpa and 1800 appm He. Both techniques show an increase of the He-to-dpa ratio up to similar to 10 dpa. At higher irradiation loads, the ratio is decreasing, which was attributed to the formation and growth of helium bubbles.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—

Projekt
<a href="/cs/project/7AMB14SK185" target="_blank" >7AMB14SK185: Studium interakcí vodíku s defekty ve strukturních slitinách pomocí pozitronové anihilační spektroskopie</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)