Composition and temperature dependence of twinning stress in non-modulated martensite of Ni-Mn-Ga-Co-Cu magnetic shape memory alloys

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216208%3A11320%2F18%3A10387822" target="_blank" >RIV/00216208:11320/18:10387822 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/18:00489254

Výsledek na webu

<a href="https://doi.org/10.1016/j.scriptamat.2017.09.046" target="_blank" >https://doi.org/10.1016/j.scriptamat.2017.09.046</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2017.09.046" target="_blank" >10.1016/j.scriptamat.2017.09.046</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Composition and temperature dependence of twinning stress in non-modulated martensite of Ni-Mn-Ga-Co-Cu magnetic shape memory alloys

Popis výsledku v původním jazyce

We study compositional and thermal dependences of lattice parameters and twinning stress sigma(TW) in Ni50-xMn25-yGa25-zCoxCuy+z magnetic shape memory alloys with non-modulated tetragonal crystal structure. The sigma(TW) was found to decrease with increasing temperature with a slope from -0.0076 to -0.0181 MPa/K. The sigma(TW) = 0.47-0.81 MPa values measured near composition-specific austenite transformation temperatures T-A were discovered to depend linearly on the c/a ratio with a slope of 14 MPa. We predict that the further decrease of c/a ratio to the level of 1.085-1.104 can result in extremely low sigma(TW) approximate to 0.1 MPa in non-modulated martensite.

Název v anglickém jazyce

Composition and temperature dependence of twinning stress in non-modulated martensite of Ni-Mn-Ga-Co-Cu magnetic shape memory alloys

Popis výsledku anglicky

We study compositional and thermal dependences of lattice parameters and twinning stress sigma(TW) in Ni50-xMn25-yGa25-zCoxCuy+z magnetic shape memory alloys with non-modulated tetragonal crystal structure. The sigma(TW) was found to decrease with increasing temperature with a slope from -0.0076 to -0.0181 MPa/K. The sigma(TW) = 0.47-0.81 MPa values measured near composition-specific austenite transformation temperatures T-A were discovered to depend linearly on the c/a ratio with a slope of 14 MPa. We predict that the further decrease of c/a ratio to the level of 1.085-1.104 can result in extremely low sigma(TW) approximate to 0.1 MPa in non-modulated martensite.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

144

Číslo periodika v rámci svazku

February 2018

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

4

Strana od-do

52-55

Kód UT WoS článku

000414824700013

EID výsledku v databázi Scopus

2-s2.0-85030837271