Temperature dependence of twinning stress of Type I and Type II twins in 10M modulated Ni-Mn-Ga martensite

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388998%3A_____%2F12%3A00377061" target="_blank" >RIV/61388998:_____/12:00377061 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.scriptamat.2012.03.012" target="_blank" >http://dx.doi.org/10.1016/j.scriptamat.2012.03.012</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.scriptamat.2012.03.012" target="_blank" >10.1016/j.scriptamat.2012.03.012</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Temperature dependence of twinning stress of Type I and Type II twins in 10M modulated Ni-Mn-Ga martensite

Popis výsledku v původním jazyce

We measure the temperature dependence of twinning stress in alloys with composition between Ni50Mn28Ga22 and Ni50Mn29Ga21 in the temperature range 288?334 K. For Type I twins, the twinning stress increases approximately linearly (0.04 MPa/K) with decreasing temperature. For Type II twins, it is temperature independent and is about 0.2 MPa. The dependences are about the same in all alloys when presented as a function of the difference between the test temperature and the martensite transformation temperature.

Název v anglickém jazyce

Temperature dependence of twinning stress of Type I and Type II twins in 10M modulated Ni-Mn-Ga martensite

Popis výsledku anglicky

We measure the temperature dependence of twinning stress in alloys with composition between Ni50Mn28Ga22 and Ni50Mn29Ga21 in the temperature range 288?334 K. For Type I twins, the twinning stress increases approximately linearly (0.04 MPa/K) with decreasing temperature. For Type II twins, it is temperature independent and is about 0.2 MPa. The dependences are about the same in all alloys when presented as a function of the difference between the test temperature and the martensite transformation temperature.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F10%2F0824" target="_blank" >GAP107/10/0824: Feromagnetické slitiny s tvarovou pamětí na bázi kobaltu</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Scripta Materialia

ISSN

1359-6462

e-ISSN

—

Svazek periodika

67

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

25-28

Kód UT WoS článku

000304851600007

EID výsledku v databázi Scopus

—