Mechanical spectroscopy of decagonal Al-Cu-Fe-Cr quasicrystalline coatings

Popis výsledku v původním jazyce

Mechanical spectroscopy measurements were performed on decagonal quasicrystalline Al-Cu-Fe-Cr coatings of three different thicknesses deposited on a mild steel substrate. The mechanical loss spectra indicate that the internal friction is mostly caused bythe quasicrystalline coating and that the contributions of both the steel substrate and the interface are small. The shear modulus measured in torsion increases with temperature, while the Young's modulus measured in flexion behaves normally. This shearmodulus anomaly is interpreted as being due to solid friction between cracked segments of the quasicrystalline coating. This phenomenon also explains the broad athermal maximum found to occur in isochronal internal friction measurements. A quantitativemodel successfully reproducing the observed behaviour has been developed. Finally, the reversible high-temperature exponential background was interpreted as being due to the onset of the brittle-to-ductile transition in the quasicrystalli

Název v anglickém jazyce

Mechanical spectroscopy of decagonal Al-Cu-Fe-Cr quasicrystalline coatings

Popis výsledku anglicky

Mechanical spectroscopy measurements were performed on decagonal quasicrystalline Al-Cu-Fe-Cr coatings of three different thicknesses deposited on a mild steel substrate. The mechanical loss spectra indicate that the internal friction is mostly caused bythe quasicrystalline coating and that the contributions of both the steel substrate and the interface are small. The shear modulus measured in torsion increases with temperature, while the Young's modulus measured in flexion behaves normally. This shearmodulus anomaly is interpreted as being due to solid friction between cracked segments of the quasicrystalline coating. This phenomenon also explains the broad athermal maximum found to occur in isochronal internal friction measurements. A quantitativemodel successfully reproducing the observed behaviour has been developed. Finally, the reversible high-temperature exponential background was interpreted as being due to the onset of the brittle-to-ductile transition in the quasicrystalli

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Philosophical Magazine

ISSN

1478-6435

e-ISSN

—

Svazek periodika

84

Číslo periodika v rámci svazku

33

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

14

Strana od-do

3571-3584

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—