Depozice uhlíkových nanostruktur v mikrovlnném výboji za atmosférického tlaku na pracovní elektrody senzorů těžkých kovů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F07%3A00019519" target="_blank" >RIV/00216224:14310/07:00019519 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/07:00308504 RIV/68081731:_____/07:00308504

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Carbon nanostructures deposition in microwave plasma torch at atmospheric pressure on sensors for heavy metal detection

Popis výsledku v původním jazyce

Carbon nanostructures were directly deposited on a working electrode of a thick film sensor used for heavy metal detection. The sensor structure (Figure 1.) was fabricated by screen-printing techniques on Al2O3 ceramic substrate. The electrodes and conductive layer material was ESL 9912-D paste and for dielectric layer ESL 4913-G paste (both ESL ElectroScience, UK). The base of working electrode is formed from Ag, Au, or Pt to prevent inter-metallic reaction with catalyst during deposition process. Demand for the electrical conductivity of the working electrode was a limiting factor for the choice of the barrier material and a metal-metal interaction during the carbon nanotubes (CNTs) deposition in high temperature (600-700 C) required an optimizationof the whole electrode system. The barrier layers were prepared by the screen printing or electroplating and possibly heated up to 500 or 850 C. The catalyst was vacuum evaporated 5-20 nm thick layer of Ni on top of the working electrode

Název v anglickém jazyce

Carbon nanostructures deposition in microwave plasma torch at atmospheric pressure on sensors for heavy metal detection

Popis výsledku anglicky

Carbon nanostructures were directly deposited on a working electrode of a thick film sensor used for heavy metal detection. The sensor structure (Figure 1.) was fabricated by screen-printing techniques on Al2O3 ceramic substrate. The electrodes and conductive layer material was ESL 9912-D paste and for dielectric layer ESL 4913-G paste (both ESL ElectroScience, UK). The base of working electrode is formed from Ag, Au, or Pt to prevent inter-metallic reaction with catalyst during deposition process. Demand for the electrical conductivity of the working electrode was a limiting factor for the choice of the barrier material and a metal-metal interaction during the carbon nanotubes (CNTs) deposition in high temperature (600-700 C) required an optimizationof the whole electrode system. The barrier layers were prepared by the screen printing or electroplating and possibly heated up to 500 or 850 C. The catalyst was vacuum evaporated 5-20 nm thick layer of Ni on top of the working electrode

Druh

D - Stať ve sborníku

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Book of Contributed Papers of The 3rd Seminar on New Trends on Plasma Physics and Solid State Physics

ISBN

978-80-89186-24-2

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

58-58

Název nakladatele

Library and Publishing Center, Comenius University, Bratislava, Slovakia

Místo vydání

Bratislava

Místo konání akce

Bratislava

Datum konání akce

4. 10. 2007

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—