Linearly graded GeSi beam-expanding/compressing X-ray monochromator
Popis výsledku v původním jazyce
In standard single-crystal V-channel germanium (220) X-ray beam-expanding/compressing monochromators for Cu K[alpha]1 radiation, a total beam expansion/compression of 5 and 10 corresponding to the asymmetry angles of 9deg and 12deg is achieved, respectively. Higher one-dimensional beam expansion/compression is achievable using larger angles of asymmetry at the expense of a decrease in the total intensity. To increase the intensity, a linearly graded Ge-rich GexSi1-x single crystal was used to prepare amonochromator with 15deg asymmetry angles (total expansion/compression factor of 21) for Cu K[alpha]1 radiation. The X-ray diffraction measurements show more than three times higher peak intensity at the output compared with that of a pure Ge monochromator.
Název v anglickém jazyce
Linearly graded GeSi beam-expanding/compressing X-ray monochromator
Popis výsledku anglicky
In standard single-crystal V-channel germanium (220) X-ray beam-expanding/compressing monochromators for Cu K[alpha]1 radiation, a total beam expansion/compression of 5 and 10 corresponding to the asymmetry angles of 9deg and 12deg is achieved, respectively. Higher one-dimensional beam expansion/compression is achievable using larger angles of asymmetry at the expense of a decrease in the total intensity. To increase the intensity, a linearly graded Ge-rich GexSi1-x single crystal was used to prepare amonochromator with 15deg asymmetry angles (total expansion/compression factor of 21) for Cu K[alpha]1 radiation. The X-ray diffraction measurements show more than three times higher peak intensity at the output compared with that of a pure Ge monochromator.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Applied Crystallography
ISSN
0021-8898
e-ISSN
—
Svazek periodika
2010
Číslo periodika v rámci svazku
43
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
3
Strana od-do
—
Kód UT WoS článku
000273764900025
EID výsledku v databázi Scopus
—