Controlled high temperature stability of microwave plasma synthesized graphene nanosheets

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F21%3A00118853" target="_blank" >RIV/00216224:14310/21:00118853 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26310/21:PU139658

Výsledek na webu

<a href="https://doi.org/10.1088/1361-6463/abdb6d" target="_blank" >https://doi.org/10.1088/1361-6463/abdb6d</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1361-6463/abdb6d" target="_blank" >10.1088/1361-6463/abdb6d</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Controlled high temperature stability of microwave plasma synthesized graphene nanosheets

Popis výsledku v původním jazyce

High temperature stability of nanomaterials plays an important role for their application in the field of nanocomposites, batteries, and sensors. Few-layer graphene nanosheets prepared by microwave plasma based decomposition of ethanol exhibited high thermal stability in the oxidation atmosphere in dependence on controlled formation of structural disorder. Analysis of differential thermogravimetry (DTG) curve profile showed three temperature regions, around 345 degrees C, 570 degrees C and above 700 degrees C, related to amorphous phase with a carbon-oxygen functional groups, small defective nanostructures and highly crystalline structure of graphene nanosheets, respectively. Raman spectroscopy and x-ray photoelectron spectroscopy (XPS) analysis of the nanosheets showed an increase of D/G Raman band ratio as well as increasing of sp(3) phase content, from 6.1 at% to 15.2 at%, for highly crystalline and highly disordered structure of the nanosheets. Thermal annealing under synthetic air was used to investigate the variation in D/G and 2D/G Raman band ratio of the samples and to estimate activation energy of oxidation and disintegration process of graphene nanosheets. The highest oxidation resistance exhibited sample with high 2D/G band ratio (1.54) and lowest oxygen content of 1.7 at%. The synthesis process led to stabilization of nanosheet structure by formation of curved edges and elimination of free dangling bonds. The nanosheets prepared in microwave plasma exhibited high surface area, over 350 m(2) g(-1), and superior thermal stability with defect activation energy in an oxidation atmosphere higher than 2 eV. Heat release rate during the oxidation process was in correlation with the amount of disorder in the samples. Fast and easy to use technique based on high power Raman spectroscopy was developed for assessment of nanomaterial oxidation resistance.

Název v anglickém jazyce

Controlled high temperature stability of microwave plasma synthesized graphene nanosheets

Popis výsledku anglicky

High temperature stability of nanomaterials plays an important role for their application in the field of nanocomposites, batteries, and sensors. Few-layer graphene nanosheets prepared by microwave plasma based decomposition of ethanol exhibited high thermal stability in the oxidation atmosphere in dependence on controlled formation of structural disorder. Analysis of differential thermogravimetry (DTG) curve profile showed three temperature regions, around 345 degrees C, 570 degrees C and above 700 degrees C, related to amorphous phase with a carbon-oxygen functional groups, small defective nanostructures and highly crystalline structure of graphene nanosheets, respectively. Raman spectroscopy and x-ray photoelectron spectroscopy (XPS) analysis of the nanosheets showed an increase of D/G Raman band ratio as well as increasing of sp(3) phase content, from 6.1 at% to 15.2 at%, for highly crystalline and highly disordered structure of the nanosheets. Thermal annealing under synthetic air was used to investigate the variation in D/G and 2D/G Raman band ratio of the samples and to estimate activation energy of oxidation and disintegration process of graphene nanosheets. The highest oxidation resistance exhibited sample with high 2D/G band ratio (1.54) and lowest oxygen content of 1.7 at%. The synthesis process led to stabilization of nanosheet structure by formation of curved edges and elimination of free dangling bonds. The nanosheets prepared in microwave plasma exhibited high surface area, over 350 m(2) g(-1), and superior thermal stability with defect activation energy in an oxidation atmosphere higher than 2 eV. Heat release rate during the oxidation process was in correlation with the amount of disorder in the samples. Fast and easy to use technique based on high power Raman spectroscopy was developed for assessment of nanomaterial oxidation resistance.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10305 - Fluids and plasma physics (including surface physics)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of physics D: Applied physics

ISSN

0022-3727

e-ISSN

1361-6463

Svazek periodika

54

Číslo periodika v rámci svazku

16

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

19

Strana od-do

„165201-1“-„165201-19“

Kód UT WoS článku

000614413600001

EID výsledku v databázi Scopus

2-s2.0-85101767769