Characterization of edge structure and misorientation between layers of microwave plasma synthesized few-layer graphene nanosheets

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F21%3A00119105" target="_blank" >RIV/00216224:14310/21:00119105 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.37904/nanocon.2020.3766" target="_blank" >https://doi.org/10.37904/nanocon.2020.3766</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.37904/nanocon.2020.3766" target="_blank" >10.37904/nanocon.2020.3766</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Characterization of edge structure and misorientation between layers of microwave plasma synthesized few-layer graphene nanosheets

Popis výsledku v původním jazyce

Topological and edge defects and misalignment of graphene layers in few-layer graphene strongly influence its chemical reactivity and thermal stability. Scanning and transmission electron microscopy and image analysis was used to determine alignment, degree of rotation, between layers in few-layer graphene prepared by decomposition of ethanol in microwave plasma torch at atmospheric pressure. The prepared nanosheets consisted of 1 to 20 layers, with interlayer distance of 0.34 nm, and the main structure was formed by successive growth of individual layers on top of each other. Using FFT, the edges and wrinkles were separated from the graphene layers themselves. The layers were spread out on each one separately and the angles of rotation between them were measured. The rotation angle between layer was from 20 to 30 degrees and the high quality graphene nanosheets, Raman bands 2D/G ratio of 1.6 and D/G ratio of 0.5, exhibited predominantly closed edges and opened edges were mostly found in the layers forming islands on the main structure. Graphene nanosheets remain fully stable in vacuum up to 1000 °C and thermogravimetric analysis showed complete burnout of the sample in synthetic air at 770 °C with more defective sample exhibiting higher weight loss between 400 and 700 °C.

Název v anglickém jazyce

Characterization of edge structure and misorientation between layers of microwave plasma synthesized few-layer graphene nanosheets

Popis výsledku anglicky

Topological and edge defects and misalignment of graphene layers in few-layer graphene strongly influence its chemical reactivity and thermal stability. Scanning and transmission electron microscopy and image analysis was used to determine alignment, degree of rotation, between layers in few-layer graphene prepared by decomposition of ethanol in microwave plasma torch at atmospheric pressure. The prepared nanosheets consisted of 1 to 20 layers, with interlayer distance of 0.34 nm, and the main structure was formed by successive growth of individual layers on top of each other. Using FFT, the edges and wrinkles were separated from the graphene layers themselves. The layers were spread out on each one separately and the angles of rotation between them were measured. The rotation angle between layer was from 20 to 30 degrees and the high quality graphene nanosheets, Raman bands 2D/G ratio of 1.6 and D/G ratio of 0.5, exhibited predominantly closed edges and opened edges were mostly found in the layers forming islands on the main structure. Graphene nanosheets remain fully stable in vacuum up to 1000 °C and thermogravimetric analysis showed complete burnout of the sample in synthetic air at 770 °C with more defective sample exhibiting higher weight loss between 400 and 700 °C.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

10305 - Fluids and plasma physics (including surface physics)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANOCON 2020: 12th International Conference on Nanomaterials - Research & Application

ISBN

9788087294987

ISSN

2694-930X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

529-534

Název nakladatele

TANGER Ltd.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

21. 10. 2020

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000664505500090