Fabrication of Al-Mg solid solution by friction stir selective alloying
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F22%3A00125096" target="_blank" >RIV/00216224:14310/22:00125096 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S0167577X21017717?dgcid=rss_sd_all#" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0167577X21017717?dgcid=rss_sd_all#</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matlet.2021.131073" target="_blank" >10.1016/j.matlet.2021.131073</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fabrication of Al-Mg solid solution by friction stir selective alloying
Popis výsledku v původním jazyce
This study reports the fabrication of an Al-Mg solid solution layer containing ∼2 at.% Mg on pure Al substrate by a solid-state processing technique called friction stir selective alloying. Accordingly, a machined groove on the surface of Al substrate was filled by a bulk Mg block and friction stir processing was applied to form Al-Mg solid solution. The XRD/EDS results revealed formation of solid solution structure in the stirred zone of the alloyed sample. Furthermore, the hardness of the prepared Al-Mg solid solution (∼55.8 HV) was more than twice greater than the hardness of the FSPed neat sample (∼25.0 HV).
Název v anglickém jazyce
Fabrication of Al-Mg solid solution by friction stir selective alloying
Popis výsledku anglicky
This study reports the fabrication of an Al-Mg solid solution layer containing ∼2 at.% Mg on pure Al substrate by a solid-state processing technique called friction stir selective alloying. Accordingly, a machined groove on the surface of Al substrate was filled by a bulk Mg block and friction stir processing was applied to form Al-Mg solid solution. The XRD/EDS results revealed formation of solid solution structure in the stirred zone of the alloyed sample. Furthermore, the hardness of the prepared Al-Mg solid solution (∼55.8 HV) was more than twice greater than the hardness of the FSPed neat sample (∼25.0 HV).
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10305 - Fluids and plasma physics (including surface physics)
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Letters
ISSN
0167-577X
e-ISSN
1873-4979
Svazek periodika
308
Číslo periodika v rámci svazku
February
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
4
Strana od-do
131073
Kód UT WoS článku
000719283900008
EID výsledku v databázi Scopus
2-s2.0-85118345299