The single crystals of Sb2-xVxTe3 (x=0.0, 0.01, 0.02, 0.03) were grown by a modified Bridgman method from elements of 5N purity. The samples were characterized by measurements of the temperature dependence of the electrical resistivity, Hall coefficient,Seebeck coefficient, thermal conductivity and magnetic susceptibility in the temperature range of 2-300 K. Magnetization curves were measured too. It was found that the vanadium-doping in the Sb2Te3 crystals does not change the concentration of holes. Asmall content of vanadium in the Sb2Te3 crystal lattice gives rise to ferromagnetic behavior at low temperatures; the Curie temperature TC increases with vanadium content and reaches approximately 22 K for Sb1.97V0.03Te3. The incorporation of V atoms into the Sb2Te3 crystal results in the suppression of the values of thermal conductivity. Substracting the electronic component of thermal conductivity we obtain the lattice thermal conductivity. At low temperatures it has an approximate T2

Název v anglickém jazyce

Some properties of the novel diluted magnetic semiconductors Sb2-xVxTe3

Popis výsledku anglicky

The single crystals of Sb2-xVxTe3 (x=0.0, 0.01, 0.02, 0.03) were grown by a modified Bridgman method from elements of 5N purity. The samples were characterized by measurements of the temperature dependence of the electrical resistivity, Hall coefficient,Seebeck coefficient, thermal conductivity and magnetic susceptibility in the temperature range of 2-300 K. Magnetization curves were measured too. It was found that the vanadium-doping in the Sb2Te3 crystals does not change the concentration of holes. Asmall content of vanadium in the Sb2Te3 crystal lattice gives rise to ferromagnetic behavior at low temperatures; the Curie temperature TC increases with vanadium content and reaches approximately 22 K for Sb1.97V0.03Te3. The incorporation of V atoms into the Sb2Te3 crystal results in the suppression of the values of thermal conductivity. Substracting the electronic component of thermal conductivity we obtain the lattice thermal conductivity. At low temperatures, it has an approximate T

Druh

D - Stať ve sborníku

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ChemZi

ISBN

1336-7242

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

84

Název nakladatele

Slovenská chemická spoločnosť pri SAV

Místo vydání

Bratislava

Místo konání akce

Tatranské Matliare

Datum konání akce

4. 9. 2005

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—