The Non-Isothermal Kinetics of Sb2S3 In (GeS2)0.2(Sb2S3)0.8 Glass
Popis výsledku v původním jazyce
The crystallization of Sb2S3 in the (GeS2)0.2(Sb2S3)0.8 glass was studied under non-isothermal conditions. The influence of the sample form on crystallization was studied using bulk sample and two fractions of powder sample. The crystallization process of the sample in the form of powder was described using autocatalytic model, the crystallization of the bulk sample was described using nucleation-growth model. The parameters of both the models were determined.
Název v anglickém jazyce
The Non-Isothermal Kinetics of Sb2S3 In (GeS2)0.2(Sb2S3)0.8 Glass
Popis výsledku anglicky
The crystallization of Sb2S3 in the (GeS2)0.2(Sb2S3)0.8 glass was studied under non-isothermal conditions. The influence of the sample form on crystallization was studied using bulk sample and two fractions of powder sample. The crystallization process of the sample in the form of powder was described using autocatalytic model, the crystallization of the bulk sample was described using nucleation-growth model. The parameters of both the models were determined.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CF - Fyzikální chemie a teoretická chemie
OECD FORD obor
—

Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)