Vliv velikosti částic na kinetiku krystalizace (GeS2)0.1(Sb2S3)0.9 skla

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F07%3A00006574" target="_blank" >RIV/00216275:25310/07:00006574 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The Particle Size Influence on Crystallization Kinetics of (GeS2)0.1(Sb2S3)0.9 Glass

Popis výsledku v původním jazyce

The dependence of crystallization process on the particle size was studied for the pseudobinary chalcogenide glass (GeS2)0,1(Sb2S3)0,9. Crystallization of Sb2S3 component was studied under isothermal and non-isothermal conditions using DSC. The strong dependence of crystallization process on the particle size was observed. With the increase of particle size the crystallization temperature range shifts to higher temperatures. This was observed for both isothermal and non-isothermal conditions. The activation energy of the process is for isothermal experiments higher than for non-isothermal experiments. The crystallization process was for all the samples described using autocatalytical model. Corresponding kinetic parameters are for crystallization underisothermal conditions lower than for non-isothermal crystallization.

Název v anglickém jazyce

The Particle Size Influence on Crystallization Kinetics of (GeS2)0.1(Sb2S3)0.9 Glass

Popis výsledku anglicky

The dependence of crystallization process on the particle size was studied for the pseudobinary chalcogenide glass (GeS2)0,1(Sb2S3)0,9. Crystallization of Sb2S3 component was studied under isothermal and non-isothermal conditions using DSC. The strong dependence of crystallization process on the particle size was observed. With the increase of particle size the crystallization temperature range shifts to higher temperatures. This was observed for both isothermal and non-isothermal conditions. The activation energy of the process is for isothermal experiments higher than for non-isothermal experiments. The crystallization process was for all the samples described using autocatalytical model. Corresponding kinetic parameters are for crystallization underisothermal conditions lower than for non-isothermal crystallization.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Thermochimica Acta

ISSN

0040-6031

e-ISSN

—

Svazek periodika

466

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

9

Strana od-do

13-21

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—