Příprava Mg0.5Ti2(PO4)3 se strukturou typu NASICON z hořečnatých borofosfátových skel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25310%2F07%3A00005838" target="_blank" >RIV/00216275:25310/07:00005838 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Preparation of NASICON-type Titanium Phosphate Mg0.5Ti2(PO4)3 from Magnesium Borophosphate Glasses
Popis výsledku v původním jazyce
Preparation of the Mg0.5Ti2(PO4)3 NASICON-type material by controlled crystallisation of magnesium titanium borophosphate glasses of the composition 30MgO.20B2O3.xTiO2.(50-x)P2O5 (x=0-25 mol% TiO2) followed by subsequent acid leaching of crystalline products was studied. All prepared glasses crystallise under heating within the temperature range of 650-870°C and the surface nucleation is the prevailing process. The lowest tendency towards crystallisation has the glass with 5 mol% TiO2. X-ray diffractionmeasurements showed that major compounds formed by glass crystallisation were Mg(PO3)2, Mg2P2O7, TiP2O7, BPO4 and Mg0.5Ti2(PO4)3. Crystalline samples, prepared by heat treatment of the glasses at 900°C, were leached with 2 m HCl aqueous solution at roomtemperature. Changes in the XRD patterns of TiO2-containing crystalline samples revealed that hydrochloric acid selectively dissolves mostly Mg2P2O7. The maximum output of Mg0.5Ti2(PO4)3 with respect to the leachability of the other phas
Název v anglickém jazyce
Preparation of NASICON-type Titanium Phosphate Mg0.5Ti2(PO4)3 from Magnesium Borophosphate Glasses
Popis výsledku anglicky
Preparation of the Mg0.5Ti2(PO4)3 NASICON-type material by controlled crystallisation of magnesium titanium borophosphate glasses of the composition 30MgO.20B2O3.xTiO2.(50-x)P2O5 (x=0-25 mol% TiO2) followed by subsequent acid leaching of crystalline products was studied. All prepared glasses crystallise under heating within the temperature range of 650-870°C and the surface nucleation is the prevailing process. The lowest tendency towards crystallisation has the glass with 5 mol% TiO2. X-ray diffractionmeasurements showed that major compounds formed by glass crystallisation were Mg(PO3)2, Mg2P2O7, TiP2O7, BPO4 and Mg0.5Ti2(PO4)3. Crystalline samples, prepared by heat treatment of the glasses at 900°C, were leached with 2 m HCl aqueous solution at roomtemperature. Changes in the XRD patterns of TiO2-containing crystalline samples revealed that hydrochloric acid selectively dissolves mostly Mg2P2O7. The maximum output of Mg0.5Ti2(PO4)3 with respect to the leachability of the other phas
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA104%2F07%2F0315" target="_blank" >GA104/07/0315: Fosfátová a borofosfátová skla dotovaná oxidy těžkých kovů pro optoelektronické a fotonické aplikace.</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Physics and Chemistry of Glasses: European Journal of Glass Science and Technology Part B
ISSN
0031-9090
e-ISSN
—
Svazek periodika
2007
Číslo periodika v rámci svazku
48(3)
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
4
Strana od-do
160-163
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—