WO3-doped zinc borophosphate glasses

Popis výsledku v původním jazyce

The effect of WO3 on the properties and structure of zinc borophosphate glasses was investigated Homogeneous glasses of the composition (100-x)[0.5ZnO-0.1B2O3-0.4P2O5].xWO3 were obtained within the concentration range of x=0-40 mol% WO3, whereas glasseswith x=45 and 50 contain microinclusions of beta-WO3. Their glass transition temperature increases with increasing WO3 content, whereas the crystallisation temperature, and the thermal stability of the glasses reveal a maximum at 10-15 mol% WO3. The structure of the glasses was studied by Raman and infrared spectroscopy, combined with 31P and 11B MAS NMR spectroscopy. The Raman spectra are characterised by a strongly polarised band at 941-930 cm-1 and a depolarised band at 832-809 cm-1, ascribed to vibrations of WO6 and W-O-W bonds, respectively. Compositional changes in the 11B MAS NMR spektra reveal a partial conversion of BO4 to BO3 units with increasing WO3 content, and the replacement of B-O-P bridges by B-O-W bridges.

Název v anglickém jazyce

WO3-doped zinc borophosphate glasses

Popis výsledku anglicky

The effect of WO3 on the properties and structure of zinc borophosphate glasses was investigated Homogeneous glasses of the composition (100-x)[0.5ZnO-0.1B2O3-0.4P2O5].xWO3 were obtained within the concentration range of x=0-40 mol% WO3, whereas glasseswith x=45 and 50 contain microinclusions of beta-WO3. Their glass transition temperature increases with increasing WO3 content, whereas the crystallisation temperature, and the thermal stability of the glasses reveal a maximum at 10-15 mol% WO3. The structure of the glasses was studied by Raman and infrared spectroscopy, combined with 31P and 11B MAS NMR spectroscopy. The Raman spectra are characterised by a strongly polarised band at 941-930 cm-1 and a depolarised band at 832-809 cm-1, ascribed to vibrations of WO6 and W-O-W bonds, respectively. Compositional changes in the 11B MAS NMR spektra reveal a partial conversion of BO4 to BO3 units with increasing WO3 content, and the replacement of B-O-P bridges by B-O-W bridges.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F07%2F0315" target="_blank" >GA104/07/0315: Fosfátová a borofosfátová skla dotovaná oxidy těžkých kovů pro optoelektronické a fotonické aplikace.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physics and Chemistry of Glasses: European Journal of Glass Science and Technology Part B

ISSN

0031-9090

e-ISSN

—

Svazek periodika

50

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—