EFFECT OF ROLLING CONTACT FATIGUE ON THE ELASTIC-PLASTIC RESPONSE OF HADFIELD STEEL

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216275%3A25510%2F15%3A39900590" target="_blank" >RIV/00216275:25510/15:39900590 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

EFFECT OF ROLLING CONTACT FATIGUE ON THE ELASTIC-PLASTIC RESPONSE OF HADFIELD STEEL

Popis výsledku v původním jazyce

zpevnění.Instrumented indentation tests were performed to study the dynamic hardening od Hadfield steel in dtifferent states of rolling-contact proces. The influence of explosion hardening, as a prospective way to improve the wear resistance of Hadfield steel, was included in the test. Each step of the degradation process was simulated using the special rolling contact stand at a defined loading condition. The measured hardness gradient of loaded surface layers displayed the depth and intensity of the induced changes. Martens hardness was measured in thus identified layers for each representative state of material. The elastic-plastic capacity of the surface layer was evaluated as a ratio elastic to the global energy of indentation. The metallography evaluation, focused on the contact surface, documented an increase of elastic response as a result of the dislocation hardening process.

Název v anglickém jazyce

EFFECT OF ROLLING CONTACT FATIGUE ON THE ELASTIC-PLASTIC RESPONSE OF HADFIELD STEEL

Popis výsledku anglicky

zpevnění.Instrumented indentation tests were performed to study the dynamic hardening od Hadfield steel in dtifferent states of rolling-contact proces. The influence of explosion hardening, as a prospective way to improve the wear resistance of Hadfield steel, was included in the test. Each step of the degradation process was simulated using the special rolling contact stand at a defined loading condition. The measured hardness gradient of loaded surface layers displayed the depth and intensity of the induced changes. Martens hardness was measured in thus identified layers for each representative state of material. The elastic-plastic capacity of the surface layer was evaluated as a ratio elastic to the global energy of indentation. The metallography evaluation, focused on the contact surface, documented an increase of elastic response as a result of the dislocation hardening process.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/TE01020038" target="_blank" >TE01020038: Centrum kompetence drážních vozidel</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2015: 24th International Conference on Metallurgy and Materials

ISBN

978-80-87294-62-8

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

845-850

Název nakladatele

TANGER, spol. s r.o.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

3. 6. 2015

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000374706100135