Vývoj lomové procesní zóny v kvazikřehkých tělesech během lomu

Popis výsledku v původním jazyce

The paper introduces a methodology for an estimation of the size and shape of a fracture process zone evolving at the macroscopic crack tip in quasi-brittle materials during their tensile failure. The procedure is based on a general description of the stress field in cracked bodies done by Williams' power series in combination with the philosophy and selected features of classical non-linear fracture models for concrete, i.e. the equivalent elastic crack models and the cohesive crack models. The proposed procedure incorporated in existing methods for the fracture parameters determination is supposed to eliminate or substantially decrease the effect of the test specimen size and geometry (the effect of the specimen's free boundaries) on the determined values of fracture characteristics of quasi-brittle materials, from which the existing methods considerably suffer. The estimation of the fracture process zone development during the fracture is illustrated on numerically simulated fractur

Název v anglickém jazyce

Development of fracture process zone in quasi-brittle bodies during failure

Popis výsledku anglicky

The paper introduces a methodology for an estimation of the size and shape of a fracture process zone evolving at the macroscopic crack tip in quasi-brittle materials during their tensile failure. The procedure is based on a general description of the stress field in cracked bodies done by Williams' power series in combination with the philosophy and selected features of classical non-linear fracture models for concrete, i.e. the equivalent elastic crack models and the cohesive crack models. The proposed procedure incorporated in existing methods for the fracture parameters determination is supposed to eliminate or substantially decrease the effect of the test specimen size and geometry (the effect of the specimen's free boundaries) on the determined values of fracture characteristics of quasi-brittle materials, from which the existing methods considerably suffer. The estimation of the fracture process zone development during the fracture is illustrated on numerically simulated fractur

Druh

D - Stať ve sborníku

CEP obor

JM - Inženýrské stavitelství

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Engineering mechanics 2009

ISBN

978-80-86246-35-2

ISSN

—

e-ISSN

—

Počet stran výsledku

12

Strana od-do

—

Název nakladatele

Neuveden

Místo vydání

Svratka, Česká republika

Místo konání akce

Svratka

Datum konání akce

11. 5. 2009

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—