Sintering behavior of feldspar rocks
Popis výsledku v původním jazyce
Sintering behaviour as dependence of water absorption, flexural strength and firing shrinkage of dry pressed test samples made from three different types of feldspar rocks on the firing temperature (1120 ? 1300 °C) was determined. Potassium, potassium-sodium and sodium-calcium industrially milled feldspars with similar granulometry according to equivalent mean spherical diameter of the grains d(0.5) in the range of 16.6 ? 20.8 microns were used. The sintering process was described according to changes in mineralogical composition of the fired test samples too. During the sintering process, feldspars gradually disappear in phases ? first of all alkali feldspars (albite, microcline); anorthite (calcium feldspar) is more resistant to melting thanks to itshigher melting temperature and it increases the sintering temperature of feldspar. Sodium-potassium feldspar Z43NaK50 with the lowest content of alkalis (3.35 % of K2O and 2.67 % of Na2O) and the highest equivalent 2mean spherical diamet
Název v anglickém jazyce
Sintering behavior of feldspar rocks
Popis výsledku anglicky
Sintering behaviour as dependence of water absorption, flexural strength and firing shrinkage of dry pressed test samples made from three different types of feldspar rocks on the firing temperature (1120 ? 1300 °C) was determined. Potassium, potassium-sodium and sodium-calcium industrially milled feldspars with similar granulometry according to equivalent mean spherical diameter of the grains d(0.5) in the range of 16.6 ? 20.8 microns were used. The sintering process was described according to changes in mineralogical composition of the fired test samples too. During the sintering process, feldspars gradually disappear in phases ? first of all alkali feldspars (albite, microcline); anorthite (calcium feldspar) is more resistant to melting thanks to itshigher melting temperature and it increases the sintering temperature of feldspar. Sodium-potassium feldspar Z43NaK50 with the lowest content of alkalis (3.35 % of K2O and 2.67 % of Na2O) and the highest equivalent 2mean spherical diamet
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA13-23051S" target="_blank" >GA13-23051S: Anortitický porcelánový střep na bázi hlinitanového cementu</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Research Inventy
ISSN
2319-6483
e-ISSN
—
Svazek periodika
4
Číslo periodika v rámci svazku
10
Stát vydavatele periodika
BD - Bangladéšská lidová republika
Počet stran výsledku
7
Strana od-do
49-55
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—