Sintering of feldspar rocks from czech quarries
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F15%3APU115654" target="_blank" >RIV/00216305:26110/15:PU115654 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Sintering of feldspar rocks from czech quarries
Popis výsledku v původním jazyce
Sintering behaviour as dependence of water absorption, flexural strength and firing shrinkage of dry pressed test samples made from three different types of feldspar rocks on the firing temperature (11201300° C) was determined. Potassium, potassiumsodiumand sodium-calcium industrially milled feldspars with similar granulometry according to equivalent mean spherical diameter of the grains d(0.5) in the range of 16.620.8 ?m were used. The sintering process was described according to changes in mineralogical composition of the fired test samples too. During the sintering process, feldspars gradually disappear in phasesfirst of all alkali feldspars (albite, microcline); anorthite (calcium feldspar) is more resistant to melting thanks to its higher meltingtemperature and it increases the sintering temperature of feldspar. Sodium-potassium feldspar Z43NaK50 with the lowest content of alkalis (3.35% of K2O and 2.67% of Na2O) and the highest equivalent mean spherical diameter d(0.5) showed t
Název v anglickém jazyce
Sintering of feldspar rocks from czech quarries
Popis výsledku anglicky
Sintering behaviour as dependence of water absorption, flexural strength and firing shrinkage of dry pressed test samples made from three different types of feldspar rocks on the firing temperature (11201300° C) was determined. Potassium, potassiumsodiumand sodium-calcium industrially milled feldspars with similar granulometry according to equivalent mean spherical diameter of the grains d(0.5) in the range of 16.620.8 ?m were used. The sintering process was described according to changes in mineralogical composition of the fired test samples too. During the sintering process, feldspars gradually disappear in phasesfirst of all alkali feldspars (albite, microcline); anorthite (calcium feldspar) is more resistant to melting thanks to its higher meltingtemperature and it increases the sintering temperature of feldspar. Sodium-potassium feldspar Z43NaK50 with the lowest content of alkalis (3.35% of K2O and 2.67% of Na2O) and the highest equivalent mean spherical diameter d(0.5) showed t
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JN - Stavebnictví
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA13-23051S" target="_blank" >GA13-23051S: Anortitický porcelánový střep na bázi hlinitanového cementu</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN
ISSN
1882-0743
e-ISSN
—
Svazek periodika
123
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
JP - Japonsko
Počet stran výsledku
6
Strana od-do
62-67
Kód UT WoS článku
000352143300011
EID výsledku v databázi Scopus
—