Behaviour of concrete in tunels and undeground concstructions in case of fire

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F14%3APU112968" target="_blank" >RIV/00216305:26110/14:PU112968 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Behaviour of concrete in tunels and undeground concstructions in case of fire

Popis výsledku v původním jazyce

The problem of cement concrete resistance to high temperatures became topical after more frequent car accidents, heavy good vehicles in particular, in tunnels with an outbreak of fire as a result of an accident. Tunnel lining is exposed to intensive temperature released as a result of fire with the temperatures high above 1000 C. The inner part of lining is exposed to various temperature intensities depending on the distance from the fire. Owing to water steam expansion in concrete as a result of temperature-time exposure, concrete surface is cracking and concrete layers are peeled off from various depths and thus the lining is secondary damaged. Appropriate composition of concrete, selection of binder of cement composite material and selection aggregate, additions and/or adding dispersed polypropylene fiber reinforcement can reduce destructive action of high temperature.

Název v anglickém jazyce

Behaviour of concrete in tunels and undeground concstructions in case of fire

Popis výsledku anglicky

The problem of cement concrete resistance to high temperatures became topical after more frequent car accidents, heavy good vehicles in particular, in tunnels with an outbreak of fire as a result of an accident. Tunnel lining is exposed to intensive temperature released as a result of fire with the temperatures high above 1000 C. The inner part of lining is exposed to various temperature intensities depending on the distance from the fire. Owing to water steam expansion in concrete as a result of temperature-time exposure, concrete surface is cracking and concrete layers are peeled off from various depths and thus the lining is secondary damaged. Appropriate composition of concrete, selection of binder of cement composite material and selection aggregate, additions and/or adding dispersed polypropylene fiber reinforcement can reduce destructive action of high temperature.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP104%2F12%2F1988" target="_blank" >GAP104/12/1988: Studium interakce složek cementových kompozitů při působení vysokých teplot</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

GECO 2014

ISBN

978-80-86407-49-4

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

85-86

Název nakladatele

Neuveden

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

25. 6. 2014

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—