EFFECT OF CURING CONDITIONS ON THE PROPERTIES OF ALKALI-ACTIVATED SLAG

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F15%3APU117332" target="_blank" >RIV/00216305:26110/15:PU117332 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

EFFECT OF CURING CONDITIONS ON THE PROPERTIES OF ALKALI-ACTIVATED SLAG

Popis výsledku v původním jazyce

Combination of fine ground granulated slag with proper alkaline activators gives alkali-activated slag (AAS) ? a material with remarkable properties. The properties of alkali-activated slag mortars are significantly affected by the curing of the samples.Due to this fact, the main aim of experimental part was to monitor the properties of AAS samples stored for various periods of time in water and in laboratory conditions (temperature 20 ? 2 °C, relative humidity 45 ? 5%). The influences of curing conditions and parameters of mechanical properties and microstructures of AAS were studied and discussed in this paper. The results indicated that the impact of wet conditions was very positive on the level of shrinkage, mechanical strength and homogeneity ofthe structure. Storage of samples in the laboratory conditions had a rather negative effect on alkali-activated slag. It was also proved by impact-echo and ultrasonic measurements.

Název v anglickém jazyce

EFFECT OF CURING CONDITIONS ON THE PROPERTIES OF ALKALI-ACTIVATED SLAG

Popis výsledku anglicky

Combination of fine ground granulated slag with proper alkaline activators gives alkali-activated slag (AAS) ? a material with remarkable properties. The properties of alkali-activated slag mortars are significantly affected by the curing of the samples.Due to this fact, the main aim of experimental part was to monitor the properties of AAS samples stored for various periods of time in water and in laboratory conditions (temperature 20 ? 2 °C, relative humidity 45 ? 5%). The influences of curing conditions and parameters of mechanical properties and microstructures of AAS were studied and discussed in this paper. The results indicated that the impact of wet conditions was very positive on the level of shrinkage, mechanical strength and homogeneity ofthe structure. Storage of samples in the laboratory conditions had a rather negative effect on alkali-activated slag. It was also proved by impact-echo and ultrasonic measurements.

Druh

D - Stať ve sborníku

CEP obor

JN - Stavebnictví

OECD FORD obor

—

Projekt

<a href="/cs/project/GA13-09518S" target="_blank" >GA13-09518S: Vliv uhlíkových nanotrubiček na zlepšení lomového chování materiálů na bázi alkalicky aktivovaných aluminosilikátových pojiv (NANOFRAM)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Geopolymers: The route to eliminate waste and emissions in ceramic and cement manufacturing

ISBN

978-1-326-37732-8

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

136-139

Název nakladatele

Societa Ceramica Italiana

Místo vydání

Bologna. Italy

Místo konání akce

Hernstein, Baden

Datum konání akce

24. 5. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—