Effect of polyethylene glycol addition on metakaolin-based geopolymer
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F16%3APU121869" target="_blank" >RIV/00216305:26110/16:PU121869 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S1877705816317672" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1877705816317672</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.proeng.2016.07.379" target="_blank" >10.1016/j.proeng.2016.07.379</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of polyethylene glycol addition on metakaolin-based geopolymer
Popis výsledku v původním jazyce
Polyethylene glycol is a non-toxic water soluble polymer often used in many industrial applications. The aim of this paper is to study the effect of polyethylene glycol with relative molecular weight ranging between 400–20000 on the properties of geopolymer mortars composed of metakaolin and sodium silicate. Polyethylene glycol was added in the amount of 0.5 to 10% by mass of metakaolin. After 28 days of curing at ambient conditions, different tests were carried out: physico-chemical (density, porosity), mechanical (flexural and compressive strength) and structural (SEM). The results showed that a maximum compressive strength of 23.9 MPa and a maximum flexural strength of 2.9 MPa were achieved by adding 10% PEG 400.reference values with higher amount of MWCNTs.
Název v anglickém jazyce
Effect of polyethylene glycol addition on metakaolin-based geopolymer
Popis výsledku anglicky
Polyethylene glycol is a non-toxic water soluble polymer often used in many industrial applications. The aim of this paper is to study the effect of polyethylene glycol with relative molecular weight ranging between 400–20000 on the properties of geopolymer mortars composed of metakaolin and sodium silicate. Polyethylene glycol was added in the amount of 0.5 to 10% by mass of metakaolin. After 28 days of curing at ambient conditions, different tests were carried out: physico-chemical (density, porosity), mechanical (flexural and compressive strength) and structural (SEM). The results showed that a maximum compressive strength of 23.9 MPa and a maximum flexural strength of 2.9 MPa were achieved by adding 10% PEG 400.reference values with higher amount of MWCNTs.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20102 - Construction engineering, Municipal and structural engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1408" target="_blank" >LO1408: AdMaS UP - Pokročilé stavební materiály, konstrukce a technologie</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
International Conference on Ecology and new Building materials and products, ICEBMP 2016
ISBN
—
ISSN
1877-7058
e-ISSN
—
Počet stran výsledku
7
Strana od-do
222-228
Název nakladatele
Elsevier
Místo vydání
neuveden
Místo konání akce
Černá Hora
Datum konání akce
31. 5. 2016
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
000387482800031