Efekt polyethylenglykolu na vlastnosti geopolymeru na bázi metakaolinu

Popis výsledku v původním jazyce

The aim of this paper is to study the effect of polyethylene glycol with relative molecular weight ranging between 400–20000 g/mol on the properties of geopolymer mortars composed of metakaolin and sodium silicate. Polyethylene glycol was added in the amount of 0.5 to 10% by mass of metakaolin. After 28 days of curing at ambient conditions, different tests were carried out: physico-chemical (density, porosity), mechanical (flexural and compressive strength). The results showed that a maximum compressive strength of 23.9 MPa and a maximum flexural strength of 2.9 MPa were achieved by adding 10% of PEG 400.

Název v anglickém jazyce

EFFECT OF POLYETHYLENE GLYCOL ADDITION ON PROPERTIES OF METAKAOLIN-BASED GEOPOLYMER

Popis výsledku anglicky

The aim of this paper is to study the effect of polyethylene glycol with relative molecular weight ranging between 400-20000 g/mol on the properties of geopolymers mortars composed of metakaolin and sodium silicate. Polyethylene glycol was added in the amount of 0.5 to 10% the mass of metakaolin. After 28 days of interpretation at ambient conditions, different tests were carried out: physico-chemical (density, of the porosity), mechanical (flexural and compressive strength). The results that showed it, and the maximum compressive strength of 14.9 MPa flexural strength and maximum of 2.9 MPa were achieved by adding 10% of PEG 400.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník abstraktů 19. odborná konference Juniorstav 2017

ISBN

978-80-214-5473-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

Neuveden

Místo vydání

Vysoké učení technické v Brně, Fakulta stavební,

Místo konání akce

Brno

Datum konání akce

26. 1. 2017

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—