QUANTIFICATION OF INFLUENCE OF MATERIAL INTERFACESTEEL-CONCRETE ON CALIBRATION CURVES FOR MODIFIED COMPACT TENSION TEST
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26110%2F17%3APU122699" target="_blank" >RIV/00216305:26110/17:PU122699 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
QUANTIFICATION OF INFLUENCE OF MATERIAL INTERFACESTEEL-CONCRETE ON CALIBRATION CURVES FOR MODIFIED COMPACT TENSION TEST
Popis výsledku v původním jazyce
Fracture properties of quasi-brittle cementitious composites are typically determined from the load–displacement or load crack open displacement response recorded during a fracture. Our contribution is focused on a numerical study prepared for a set of experimental tests, which are used to study the fracture behaviour on notched dog-boneshaped specimens made of cementitious materials. These specimens are subjected to modified compact tension (ModCT) test under a specific range of eccentricity of the tensile load. The aim is to introduced the K-calibration, T-stress and COD curves for ModCT specimens and their accuracy for various ratio of interface steel/concrete is discussed.
Název v anglickém jazyce
QUANTIFICATION OF INFLUENCE OF MATERIAL INTERFACESTEEL-CONCRETE ON CALIBRATION CURVES FOR MODIFIED COMPACT TENSION TEST
Popis výsledku anglicky
Fracture properties of quasi-brittle cementitious composites are typically determined from the load–displacement or load crack open displacement response recorded during a fracture. Our contribution is focused on a numerical study prepared for a set of experimental tests, which are used to study the fracture behaviour on notched dog-boneshaped specimens made of cementitious materials. These specimens are subjected to modified compact tension (ModCT) test under a specific range of eccentricity of the tensile load. The aim is to introduced the K-calibration, T-stress and COD curves for ModCT specimens and their accuracy for various ratio of interface steel/concrete is discussed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20102 - Construction engineering, Municipal and structural engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1408" target="_blank" >LO1408: AdMaS UP - Pokročilé stavební materiály, konstrukce a technologie</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Modelování v mechanice 2017
ISBN
978-80-248-4010-9
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
1-8
Název nakladatele
Neuveden
Místo vydání
Ostrava, Česká republika
Místo konání akce
Ostrava
Datum konání akce
19. 1. 2017
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—