Injection Moulding and Sintering of Ceria Ceramics

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F02%3APU27189" target="_blank" >RIV/00216305:26210/02:PU27189 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Injection Moulding and Sintering of Ceria Ceramics

Popis výsledku v původním jazyce

Ceria powder was dry-milled to sub-micrometric particle sizes and used in the preparation of ceramic mixture for injection moulding. Specimen bodies were injection moulded in the shape of rectangular bars. The sintering kinetics of these bodies was studied in a dilatometer under various sintering conditions and also by the rate-controlled sintering method. Sintering the injection moulded CeO2 to a density of 7.08 g.cm-3 (99.3% TD) was possible already at a temperature of 1400°C, and the highest densityvalue (99.8% TD) was obtained at a heating rate of 2°C.min-1 and a holding time of 1 hour at 1500°C. Using heating rates of over 5°C.min-1 had an adverse effect on the density obtained. Applying the rate-controlled sintering (RCS) method did not lead toany decrease in the grain size if compared with temperature-controlled sintering (TCS).

Název v anglickém jazyce

Injection Moulding and Sintering of Ceria Ceramics

Popis výsledku anglicky

Ceria powder was dry-milled to sub-micrometric particle sizes and used in the preparation of ceramic mixture for injection moulding. Specimen bodies were injection moulded in the shape of rectangular bars. The sintering kinetics of these bodies was studied in a dilatometer under various sintering conditions and also by the rate-controlled sintering method. Sintering the injection moulded CeO2 to a density of 7.08 g.cm-3 (99.3% TD) was possible already at a temperature of 1400°C, and the highest densityvalue (99.8% TD) was obtained at a heating rate of 2°C.min-1 and a holding time of 1 hour at 1500°C. Using heating rates of over 5°C.min-1 had an adverse effect on the density obtained. Applying the rate-controlled sintering (RCS) method did not lead toany decrease in the grain size if compared with temperature-controlled sintering (TCS).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20525.10" target="_blank" >OC 525.10: Příprava a vlastnosti keramických materiálů s iontovou nebo iontově-elektronovou vodivostí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics International

ISSN

0272-8842

e-ISSN

—

Svazek periodika

28

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

337-344

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—