Vliv slinovacího cyklu na mikrostrukturu oxidových keramických materiálů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU51694" target="_blank" >RIV/00216305:26210/05:PU51694 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of sintering schedule on grain size of oxide ceramics

Popis výsledku v původním jazyce

The sintering and grain size of sub-micrometric CeO2 and ZrO2 + 3 mol%Y2O3 prepared by injection moulding and cold isostatic pressing were studied. Using combinations of the ceramic powders used and shaping methods, three types of bodies were prepared that were characteristic by their own green body microstructure. Their sintering behaviour was described with the aid of high-temperature dilatometry. Each type of specimen was then sintered to two levels of final density (higher than 98% t.d.), for eeachdensity always via two or three different firing modes differing in temperature and holding time. In the ZrO2 specimen it was verified statistically that the final grain size was the same irrespective of whether the given final density was obtained by sintering for a longer period at a lower temperature or for a shorter period at a higher temperature. This finding did not hold for the injection moulded CeO2 cylinders, which contained cavities in the order of millimetre. When these defect

Název v anglickém jazyce

Effect of sintering schedule on grain size of oxide ceramics

Popis výsledku anglicky

The sintering and grain size of sub-micrometric CeO2 and ZrO2 + 3 mol%Y2O3 prepared by injection moulding and cold isostatic pressing were studied. Using combinations of the ceramic powders used and shaping methods, three types of bodies were prepared that were characteristic by their own green body microstructure. Their sintering behaviour was described with the aid of high-temperature dilatometry. Each type of specimen was then sintered to two levels of final density (higher than 98% t.d.), for eeachdensity always via two or three different firing modes differing in temperature and holding time. In the ZrO2 specimen it was verified statistically that the final grain size was the same irrespective of whether the given final density was obtained by sintering for a longer period at a lower temperature or for a shorter period at a higher temperature. This finding did not hold for the injection moulded CeO2 cylinders, which contained cavities in the order of millimetre. When these defect

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Science

ISSN

0022-2461

e-ISSN

—

Svazek periodika

40

Číslo periodika v rámci svazku

11

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

9

Strana od-do

5581-5589

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—