Electrophoretic deposition of alumina and zirconia I. Single-component system

Popis výsledku v původním jazyce

Electrophoretic deposition of Al2O3 and ZrO2 suspended in isopropanol in the presence of monochloroacetic acid and polyvinylbutyral under constant-current conditions was studied. The deposition of ceramic particles occurred on the anode. An optimum deposition in terms of surface flatness, deposit density and thickness was found for 15 wt.% of monochloroacetic acid in isopropanol. The electrophoretic mobility of alumina particles in this suspension was determined from deposition kinetics. The sintering bbehaviour, hardness, fracture toughness and bending strength of Al2O3 and ZrO2 electrophoretic deposits were comparable with the values measured for the specimens prepared from identical powders by injection moulding and cold isostatic pressing or with the values given in the literature.

Název v anglickém jazyce

Electrophoretic deposition of alumina and zirconia I. Single-component system

Popis výsledku anglicky

Electrophoretic deposition of Al2O3 and ZrO2 suspended in isopropanol in the presence of monochloroacetic acid and polyvinylbutyral under constant-current conditions was studied. The deposition of ceramic particles occurred on the anode. An optimum deposition in terms of surface flatness, deposit density and thickness was found for 15 wt.% of monochloroacetic acid in isopropanol. The electrophoretic mobility of alumina particles in this suspension was determined from deposition kinetics. The sintering bbehaviour, hardness, fracture toughness and bending strength of Al2O3 and ZrO2 electrophoretic deposits were comparable with the values measured for the specimens prepared from identical powders by injection moulding and cold isostatic pressing or with the values given in the literature.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics International

ISSN

0272-8842

e-ISSN

—

Svazek periodika

30

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

10

Strana od-do

843-852

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—