Alumina and Zirconia Based Layered Composites: Part 1 Preparation
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU86098" target="_blank" >RIV/00216305:26210/09:PU86098 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/09:00332703
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Alumina and Zirconia Based Layered Composites: Part 1 Preparation
Popis výsledku v původním jazyce
Electrophoretic deposition of Al2O3 and ZrO2 powders from isopropanol suspension in the presence of monochloroacetic acid under constant-current conditions was studied. The similar charge and electrophoretic mobility of Al2O3 and ZrO2 in the suspensionswas found. Adjusting to properly controlled kinetics of deposition deposits were prepared of pre-defined thicknesses. In view of the negative charge of Al2O3 and ZrO2 particles in the isopropanol suspensions used, the prepared layers were deposited on the anode and thus they were not affected by possible solvent electrolysis, which contributed to their defect-free and low-porosity structure.
Název v anglickém jazyce
Alumina and Zirconia Based Layered Composites: Part 1 Preparation
Popis výsledku anglicky
Electrophoretic deposition of Al2O3 and ZrO2 powders from isopropanol suspension in the presence of monochloroacetic acid under constant-current conditions was studied. The similar charge and electrophoretic mobility of Al2O3 and ZrO2 in the suspensionswas found. Adjusting to properly controlled kinetics of deposition deposits were prepared of pre-defined thicknesses. In view of the negative charge of Al2O3 and ZrO2 particles in the isopropanol suspensions used, the prepared layers were deposited on the anode and thus they were not affected by possible solvent electrolysis, which contributed to their defect-free and low-porosity structure.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F06%2F0724" target="_blank" >GA106/06/0724: Mikrostrukturně indukované stínící efekty při porušování kompozitů s keramickou matricí</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials
ISSN
1013-9826
e-ISSN
—
Svazek periodika
412
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
—
Kód UT WoS článku
000272077000036
EID výsledku v databázi Scopus
—